✍ Scribed by Alexander V. Mazur; Michael M. Gasik
No coin nor oath required. For personal study only.
Thermal expansion of CVD single crystal silicon was measured with a push-rod dilatometer up to 1100 • C for different crystallographic orientations of the specimen. Thermal analysis, Laue analysis and X-ray diffraction were used to verify silicon crystal orientation and absence of possible phase transformations. Coefficients of technical thermal expansion have been calculated in this temperature range and their variations with temperature have been demonstrated. These differences might cause anisotropy in thermal stresses, which has been calculated and compared with experimental values of dry-oxidised silicon wafers.
📜 SIMILAR VOLUMES
Both, the normal strength concretes (NSC) and high strength concretes (HSC) have been used in structures which may be exposed to elevated temperatures. Concretes have also been used in the construction of radiation shielding structures. Data on the behaviour of concrete at high temperature is of pri
The speed of sound u has been measured in {(1x 2 )C 2 H 6 + x 2 CO 2 }, with x 2 ≈ 0.6, along seven isotherms at temperatures between T = 220 K and T = 450 K by means of a spherical resonator. The greatest pressure on each isotherm was approximately p = 1.2 MPa except at T = 220 K where, to avoid co
Measurements of molar enthalpy increments for (0.5H 2 O + 0.5C 2 H 5 OH) are reported. A counter-current water-cooled flow calorimeter was used to measure 76 enthalpy increments over the temperature range 373.2 K to 573.2 K at pressures from 0.1 MPa up to 11.3 MPa. Extrapolation of the gas phase mea
The phase behaviour of binary mixtures of dimethyl ether with nitrogen, or argon, or krypton, or xenon as the second non-polar component has been investigated at temperatures from T = (270 to 110) K and at pressures up to 200 MPa. The measurements were performed in an optical high-pressure cell, fit