The Structure of the Free Volume in Poly(styrene-co-acrylonitrile) from Positron Lifetime and Pressure Volume Temperature (PVT) Experiments

✍ Scribed by Günter Dlubek; Jürgen Pionteck; Duncan Kilburn

• Publisher: John Wiley and Sons
• Year: 2004
• Tongue: English
• Weight: 232 KB
• Volume: 205
• Category: Article
• ISSN: 1022-1352
• DOI: 10.1002/macp.200300103

✦ Synopsis

Abstract

Summary: The structure of the free volume and its temperature dependence between 25 and 190 °C of copolymers of styrene with acrylonitrile, SAN (0 to 50 mol‐% AN), is studied by pressure volume temperature (PVT) experiments and positron annihilation lifetime spectroscopy (PALS). In this first part of the work, PVT data are reported which were analysed with the Simha‐Somcynsky equation of state (S‐S eos) to estimate the volume fraction of holes, h, which constitute the excess free volume. The temperature and pressure dependence of the specific volume V, the specific occupied and free volume, V~occ~ = (1 − h)V and V~f~ = hV, and the corresponding isobaric expansivities and isothermal compressibilities for both the rubbery and glassy state, are estimated. We obtained the unexpected results that (i) the occupied volume changes its coefficient of thermal expansion at T~g~ from α~occ,g~ ≈ 0.5__α__~g~ ≈ 1 × 10^−4^ K^−1^ below T~g~ to almost zero above T~g~ and (ii) the isothermal compressibility of the occupied volume at zero pressure is rather high, κ~occ~ ≈ 2 × 10^−4^ MPa^−1^, and decreases only slightly at T~g~. The variation of total, occupied, and free volume parameters with the composition of the SAN copolymers is discussed.

Specific volume V of SAN50 as a function of temperature T and as selection of isobars (in MPa).

magnified imageSpecific volume V of SAN50 as a function of temperature T and as selection of isobars (in MPa).