Rough estimates are made of the stress necessary to force a dislocation through a Guinier-Preston zone in an aluminum alloy containing 2 at. o/0 copper and in an aluminum alloy containing 13 at. o/0 silver. The values found are significantly less than those calculated using a model for the strength of a precipitation hardened alloy proposed by Orowan. It is suggested that the process of shearing the zones determines the initial flow-stress in these age-hardening alloys. LA Rl%ISTANCE D'UN ALLIAGE CONTENANT DES ZONES Les auteurs ont d&ermine t&s approximativement la tension n&essaire pour forcer une dislocation 8. traverser une zone de Guinier-Preston dans un alliage d'aluminium-cuirvre (20/o en concentration atomique) et un alliage aluminium-argent (13% en concentration atomique). Las valeurs trouv&es sont nettement infbrieures it celles calcul&es sur la base du mod&le propo& par Orowan pour la d&termination de la r&istance d'un alliage durci par pr8cipitation. Les auteurs suggerent que le pro&d& de cisaillement des zones d&ermine, dans ces alliages durcis par vieillissement, la valeur de la tension n&essaire B I'initiation du mouvement des dislocations. DIE FESTIGKEIT EINER LEGIERUNG MIT GUINIER-PRESTON-ZONEN Es werden grobe Abschtitzungen derjenigen Spannung gegeben, die eiue Versetzung zum Schneiden einer Guinier-Preston-Zone zwingt, und zwar fiir Legierungen von Al mit zwei Atom o?0 Cu und van Al mit 13 Atom O/J Ag. Die berechneten Spannungen sind merklich kleiner als diejenigen, welche sich fiir ein anderes Model1 ergeben, das von Orowan fiir die Ausscheidungsverfestigung eingefiihrt wurde. Es wird daher vorgeschlagen, dass die Scherung der G.P.-Zonen die Fliessgrenze dieser Legierungen bestimmt.
π SIMILAR VOLUMES