The role of hydrogen embrittlement in crack propagation in corrosion fatigue of steels

โœ Scribed by V. A. Marichev; S. A. Shipilov

Publisher
Springer
Year
1987
Tongue
English
Weight
159 KB
Volume
23
Category
Article
ISSN
1573-885X

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

Mechanism of corrosion fatigue crack pro
Mechanism of corrosion fatigue crack propagation in high strength steels
โœ Nakasa Keijiro; Takei Hideo; Itoh Hisashi ๐Ÿ“‚ Article ๐Ÿ“… 1983 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 922 KB

The crack propagation velocity in corroGon fatigue (du/dN), were measured on the Ni-Cr-Mo steel quenched and tempered at 473 or 773 K. The steel with high sensitivity to delayed failure reveals the largest (du/dN), under square load and the smaller (da/dN), under positive saw tooth load. The frequen

Crack nucleation and propagation of corr
Crack nucleation and propagation of corrosion fatigue in high-strength steel
โœ Y Hirose; T Mura ๐Ÿ“‚ Article ๐Ÿ“… 1985 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 851 KB

Crack nucleation and growth behavior of corrosion fatigue are investigated experimentally and theoretically for 200ยฐC tempered AISI 4340 steel in 35% NaCl solution. The crack nucleation at notch roots is determined by the electrical potential method. The cycle for crack nucleation, N,, increases wit