The radial selectivity of in-situ core-doped crystal rods grown by the double die EFG method
✍ Scribed by Prof. Dr. P. Rudolph; K. Shimamura; Prof. Dr. T. Fukuda
- Publisher
- John Wiley and Sons
- Year
- 1994
- Tongue
- English
- Weight
- 406 KB
- Volume
- 29
- Category
- Article
- ISSN
- 0232-1300
No coin nor oath required. For personal study only.
✦ Synopsis
The Radial Selectivity of In-situ Core-doped Crystal Rods Grown by the Double Die EFG Method
The radial selectivity of in-situ core-doped Cr, Nd: LiNbO, crystal rods, grown by the double die EFG (edge-defined film fed growth) method, has been investigated. Two crucibles are combined with an outer and inner die for ascending of different doped melts. The critical growth parameters affected by the diffusion depended spreading effect of the dopant within the melt meniscus have been estimated. The first experimental tests show a good agreement with the theoretical prediction. Single crystalline LiNbO, rods with a length of about 100 mm and an outer diameter of 5 mm consisting of sharp separated inner Cr-or Nd-doped core region with diameters between 1.5 and 4 mm were grown successfully.
Es wurde die rddiale Selektivitat von in-situ dotierten Cr, Nd : LiNbO, Kristallstibchen untersucht, die mit der EFG (edge-defined film fed growth) methode rnit einem Doppelformgeber gezuchtet wurden. Der Doppeltiegel wurde mit einen doppelten Formgeber versehen, um zwei unterschiedlich dotierte Schmelzen gleichzeitig aufsteigen zu lassen. Es wurden die kritischen Ziichtungsparameter in Abhangigkeit von der diffusiv bedingten.Mischung im Schmelzmeniskus abgeschitzt. Die ersten experimentellen Ergebnisse zeigen eine gute Ubereinstimmung rnit den theoretischen Voraussagen. Es wurden einkristalline LiNbO, Stabchen mit einer Lange von etwa 100 mm und einem 2uDeren Durchmesser von 5 mm gezogen, die eine scharfe separierte Cr oder Nd dotierte Seele rnit Durchmessern zwischen 1.5 und 4 mm enthielten.