✍ Scribed by A.A Zhukov; R.L Snezhnoi
No coin nor oath required. For personal study only.
Fe-C alloys and in diamond at different temperatures the iron-diamond equilibrium diagram at atmospheric pressure has been plotted. The shift of the diamond liquidus with varying pressure has been studied. It is shown that with the transition from high to low pressure the 1 *Fe& + Fe& eutectic is being replaced by the 1 *Fe& + diamond eutectic. At atmospheric pressure the dome of the cementite liquidus either conserves a slightly open maximum (variant A), or is being overlapped by the diamond liquidus, so that the cementite maximum becomes slightly hidden and the 1 =? Fe& + diamond eutectic transformation is replaced by the peritectic transformation 1 + diamond ri: 1 + Fe& (variant B). Both variants are computed. On the basis of results obtained certain indirect data ooncerning the partial mole volume of carbon in liquid Fe-C alloys are being reconsidered. LE SYSTEME FER-CARBONE. NOUVEAUX Rl%ULTATS-III. LE DIAGRAMME DE PHASE FER-DIAMANT La construction du liquidus du diemant sur le diagramme de phase fer-diamant h pression ordineire s Bt6 effectu6a B psrtir de la comperaison des activit6s du carbone dens les 8lh8ges liquides Fe-C sur-satur6s et dens le diament i diverses tempbratures. Le d6plaaement du liquidus du diamant sous l'influence de la pression a BtB Btudi6. On a montr6 qu'avec le passage des hautes pressions e la pression atmospherique l'euteotique 1 s Fe& + Fe,C, est remplace par l'eutactique 1 e Fe& + diament. Aveo cel& la coupole du liquidus de la c6mentite soit conserve un maximum lbgitrement ouvert (varianta A), on bien elle est recouverte par le liquidus du diamant et alors le maximum devient 16gerement cach6, la transformation eutectique 1 *Fe& + diament est tr8nsmutC en trsnsformation peritectique 1 + diamant s 1. + Fe,C (varianti B). Lee dew variantes sont calcul8es. Se fondant sur les rbultats obtenus certaines don& indirectes sent revis& p8r exemple le volume moleire partiel du carbone dam les alliages liquides Fe-C. DAS SYSTEM EISEN-KOHLENSTOFF. NEUE ENTWICKLUNGEN-III. DAS EISEN-DIAMANT ZUSTANDSDIAGRAMM Beim Vergleich der Kohlenstoffektiviti%ten in den iiberrhttigten 5tiigen Fe-C-Le&ungen und in Diamant bei verschiedenen Tempenrturen wird des Eisen-Diam8nt Zustandsdiagnunm beim Atmospbivendruck aufgebaut. Die Verschiebung des Diamantliquidus mit dem Druck wurde untersucht. Es hat eich herausgestellt, daD mit dem vbergeng von hohen zu den niedrigen Drucken das Eutektikum 1 e Fe& + Fe&, durch das Eutektikum 1 Y? Fe& + Diamant ers&zt wird. 33&n Atmosph&rendruck beh< d8s Zementitliquidus entweder ein leicht offenes Maximum bei (Varianta A), oder es wird vom Diamantliquidus 0tW8S iiberlagert, so da5 das Zementitmaximum zum Teil verdeckt wird, und die eutektische Umwandlung 1 s Fe& + Diamant durch eine peritektische Umwandlung 1 + Diamant ?r 1 + Fe& ersetzt wird (Varier& B). Beide Varianten sind durchgerechnet. Auf de: Basis der gewonnen Ergebnisse wurden einige indirekte Angaben, die sich auf dss pertielle Mol-Volumen des Kohlenstaffs in den fliissigen Fe-C-Legierunugen beziehen, revidiert.
📜 SIMILAR VOLUMES