3 'A silicon iron in the pre-yield microstrain region, slip bands are nucleated at grain boundaries.
The conditions which determine whether they propagate across a grain are elucidated.
A simple model is proposed to explain the characteristics of those slip bands which are nucleated at applied stresses insufficient to propagate them across the grains. LA FORMATION DES BANDES DE GLISSEMENT DANS LE FER 3% SILICON POLYCRISTALLIN DANS LA REGION DES MICRODEFORMATIONS PRESENTS A LA LIMITE ELASTIQUE Les auteurs montrent que des bandes de glissement apparaissent aux joins des grains dans la region de microd&formation, au tours d'essais de traction de fer polycristallin contenant 3% de silicium. 11s ont pu &cider les conditions qui dbterminent la propagation de ces bandes ZL travers les grains. 11s proposent un modele simple pour expliquer les caract&istiques des bandes de glissement qui apparaissent lorsque les tensions appliqubes sont insuffisantes pour permettrent leur propagation B travers le grain. DIE BILDUNG VON GLEITBANDERN IN POLYKRISTALLINEM 3 %-SILIZIUM-EISEN IM GEBIET DER MIKRODEHNUNG VOR DEM FLIESSEN Bei Zugversuchen an polykristallinem Eisen mit 3% Silizium werden im Gebiet der Mikrodehnung vor dem FlieDen an Korngrenzen Gleitbiinder gebildet. Es werden die Bedingungen gekliirt, die bestimmen, ob sie sich iiber ein Korn ausbreiten oder nicht. Ein einfaches Model1 wird ZUP Erkliirung der Eigenschaften solcher Gleitbiinder vorgeschlagen, bei denen die angelegte Spannung zwar zur Bildung, nicht aber zur Ausbreitung iiber das Korn ausreicht.
๐ SIMILAR VOLUMES