The formation of point defects during deformation of aluminum and their subsequent annealing behavior
✍ Scribed by H.B Aaron; H.K Birnbaum
- Publisher
- Elsevier Science
- Year
- 1965
- Weight
- 912 KB
- Volume
- 13
- Category
- Article
- ISSN
- 0001-6160
No coin nor oath required. For personal study only.
✦ Synopsis
The formation of point defects during plastic deformation and their subsequent interactions with dislocations were studied in high purity aluminum using a low temperature strain aging technique. It w&s shown that a point defect was formed at 77'K whose energy of motion was about a.09 eV and that the interaction of this defect with dislocations gave rise to a yield point. The kinetics of strain aging were studied and compared to the results previously reported for copper. The mechanism of strain aging and the dislocation-point defect i&xactions appear to be quite similar for aluminum and copper.
The low temperature strain aging technique was used to examine the mechanisms of formation of point defects during deformation of single crystals of aluminum and Cu + 0.5 at.% Au. It was shown that the major source' of point defects was jogs produced by intersection of dislocations on the primary and conjugate slip systems.
LA FORMATION DE DEFAUTS PONCTUELS PENDANT LA DEFORMATION DE L'ALUMINIUM ET LEUR COMPORTEMENT AU COURS D'UN RECUIT SUBSEQUENT Les auteurs
Btudient la formation de dbfauts ponctuels au tours de la d&formation plastique et leurs interactions ult&ieures avec les dislocations dens de l'aluminium t&s pur, en utilisant une technique de vieillissement de deformation Q basse tempbrature. 11 apparait qu'un dbfaut ponctuel est c&6 rl 77°K avec une 6nergie de mouvement d'environ 0,09 eV et dont l'interaction avec les dislocations donne lieu B un accident & la limite Blastique. 11s Btudient la cin&ique du vieillisaement de d&formation et comparent aux rbsultats publi& pr&&demment pour le cuivre. Le mbcanisme du viellissement de dbformation et les interactions dislocation-d6faut ponctuel apparaisaent comme &ant entibrement semblables pour l'aluminium et le cuivre. Les auteurs utilisent la technique du viellissement de d&formation & baese temp&ature pour examiner les m6canismes de formation de dbfauts ponctuels pendant la d&formation de monocristaux d'aluminium et Cu + 0,6% at. Au. 11s montrent que les dbfauts ponctuels proviennent principalement des crans produits par l'intersection de dislocations sur les systbmes de glisaement primaire et conjugu& DIE BILDUNG VON PUNKTFEHLERN W&REND DER VERFORMUNG VON ALUMINIUM UND IHR ANSCHLIEBENDES AUSHEILVERHALTEN Die Bildung von Punktfehlern w&hrend der plastischen Verformung und ihre anschlienenden Wechselwirkungen mit Versetzungen wurden in hochreinem Aluminium mittles Anlessen unter Last bei tiefen Temperaturen untersucht. Es wurde gezeigt, da0 bei 77'K eine Fehlstelle erzeugt wird, deren Wanderungsenergie etwa 0.09 eV ist, und da6 die Wechselwirkung dieser Fehlstelle mit Versetzungen AnlaI3 zu einer FlieBgrenze geben. Die Kinetik des Anlassens unter Last wurde untersucht und die Ergebnisse werden verglichen mit den friiheren Daten fiir Kupfer. Der Mechaniimus des Anlassens unter Last, sowie die Wechselwirkungen zwischen Versetzungen und Punktfehlern scheinen fiir Aluminium und Kupfer iihnlich zu sein. Die Tieftemperaturalterungstechuik wurde benutzt zur Untersuchung der Mechanismen der Punktfehlererzeugung wiihrend der Verformung von Aluminium-und Cu + 0.5 At.-% Au-Einkristallen. Es zeigte sich, daIj die Hauptquelle fiir Punktfehler Versetzungsapriinge waren, die durch den Schnitt von Versetzungen in den primiiren und konjugierten Gleitsystemen erzeugt wurden.