The elastic moduli of quenched binary solid solutions of aluminum, bismuth, cadmium, indium, lead, lithium, silver, tin and zinc in magnesium have been measured and the results considered with reference to previous lattice parameter measurements. A simple variation with electron-atom ratio reveals no effects of Brillouin zone overlaps and earlier work invoking these is discussed in the light of the results. The decreasing modulus as the electron-atom ratio is increased may be explained in terms of a screening effect of the conduction electrons.
PROPRIETES
ELASTIQUES DES SOLUTIONS SOLIDES DE MAGNESIUM Les modules Blastiques des solutions solides binaires trempees d'aluminium, de bismuth, de cadmium, d'indium, de plomb, de lithium, d'argent, d'&ain et de zinc dans le magn6sium ont 6th mesu&, et les r&sultats ont 6tB examines en se rapportant aux mesures antbrieures des param&tres de r6seaux. Une variation simple avec le rapport 6lectron-atome ne met en bvidence aucun des effets de chevauchement des zones de Brillouin, et le travail p&&dent invoquant ceux-ci est discutb ?I la IumiBre de ces r6sultats. Le fait que le module diminue quand le rapport 6lectron-atome augmente peut &re interpr&& en considerant un effet d'6cran des Electrons de conduction. DIE ELASTISCHEN EIGENSCHAFTEN VON MAGNESIUM-LEGIERUNGEN Die Elastizit&tsmoduln abgeschreckter biniirer Legierungen von Aluminium, Wismut, Kadmium, Indium, Blei, Lithium, Silber, Zinn und Zink mit Magnesium wurden gemessen und die Ergebnisse in Hinblick auf neuere Gitterparametermessungen diskutiert. Eine einfache Anderung mit den e/a-Ver-h<nis zeigt keine Einfliisse van Brillouinzoneniiberlappungen und eine friihere Arbeit, die devon Gebrauch macht, wird im Licht der neuen Ergebnisse diskutiert. Der mit zunehmendem e/o-Verhiiltnis abnehmende Modul kann mit Abschirmungseffekten der Leitungselektronen gedeutet werden.