The effect of mechanical deformation on magnetic properties and MRI artifacts of type 304 and type 316L stainless steel

✍ Scribed by Lee P. Bendel; Frank G. Shellock; Mark Steckel

• Publisher: John Wiley and Sons
• Year: 1997
• Tongue: English
• Weight: 737 KB
• Volume: 7
• Category: Article
• ISSN: 1053-1807
• DOI: 10.1002/jmri.1880070635

✦ Synopsis

The purpose of this study was to evaluate the influence of composition and deformation of biomedical stainless steels on mechanical properties, magnetic properties, and MRI artifacts. Type 304 and Type 316L samples were prepared using standard wire-drawing techniques. Mechanical properties were determined using standard test methods. The amount of ferromagnetic phase present was estimated using a Severn Gage and x-ray diffraction. Magnetic field attraction and artifacts were determined using previously described techniques. The strength of both steels increased significantly with increasing deformation. None of the type 316L wires transformed to the magnetic phase. The amount of magnetic phase in the type 304 wires increased with increasing deformation. There was no magnetic field attraction, and artifacts were minimal for all of type 316L wires and the undeformed type 304 wire. Deflection and artifacts were significant for the deformed type 304 stainless steel. These results provide guidance regarding the use of type 304 and type 316L stainless steels for bioimplants. In this regard, type 316L stainless steel seems to be a more acceptable material with respect to MR compatibility.