The effect of corona discharge treatment of ethylene copolymers on their adhesion to aluminum

✍ Scribed by T. Hjertberg; B.-Å Sultan; E. M. Sörvik

• Publisher: John Wiley and Sons
• Year: 1989
• Tongue: English
• Weight: 1010 KB
• Volume: 37
• Category: Article
• ISSN: 0021-8995
• DOI: 10.1002/app.1989.070370503

✦ Synopsis

The efficiency of different techniques to obtain improved adhesion in polyethylene-aluminum laminates have been studied. Both surface treatments, such as thermal oxidation and corona discharge, and the use of copolymers with polar comonomers, i.e., vinyl acetate (EVA) and butyl acrylate (EBA), have been included. Thermal oxidation performed by high temperature extrusion including an ozone shower seems to be more effective than corona discharge. In a model experiment thermal oxidation was studied in more detail. The adhesion, as measured by a T-peel test, increased with the content of carbonyl measured by reflexion IR, except for relatively long thermal treatments. In the latter case molecular scission gave a large fraction of low molecular weight material with low cohesive strength. For EBA and EVA the peel strength increased linearly with the bulk concentration of comonomer from about 100 N/m for untreated polyethylene to 450 and 300 N/m, respectively, at 5 mol I % comonomer. Corona discharge treatment of these copolymers had, however, a most remarkable effect on the adhesion properties. The increases, relative to untreated EBA and EVA, were much more dramatic compared to polyethylene, e.g., three to four and less than two times, respectively. The higher values obtained with EBA are suggested to be due to the conversion of acrylate groups into carboxylic acid. In the case of EVA, loss of acetic acid might instead decrease the content of polar groups.