The correlation between the corrosivity and the atomic structure of grain boundaries in copper was investigated by measuring the corrosion rate of about lO.Oa, boundaries of different structures in an aqueous solution of HCI and Feel, as a function of the orientation reiationship. Ideal low energy boundaries showed no boundarv corrosion at all. The boundary corrosivity increased to the value of random boundaries if the deviation was less than one degree. The corrosion process was found to initiate and proceed in channels along dislocations in grain boundaries.
R&urn&-Nous avons 6tudi6 la correlation entre la corrosivitP et la structure atomique des joints de grains dans le cuivre en mesurant la vi&es-se de corrosion d'environ 1O.UOO joints de dilT&entts structures dans une solution solide aqueuse d'HC1 et de Feel, en fonction des relations &orientation. Les joints parfaits de faible tnergie ne prisentaient pas du tout de corrosion intertranuiaire. La corrosivith dcs joints augmentait jusqu'g la vaieur des joints aleatoires pour une deviation infkrieure g un degri. Le ph&omZne de corrosion debutait et se poursuivait ie long de dislocations intergranulaires. Zusammenfassung-Die Korrelation von Korrosionsverhalten und atomarer Struktur van Korngrenzen wurde an Kupfer untersucht. Die Korrosionsrate wurde an rund 10 000 Korngrenzen unrerschiedlicher Struktur in einer wLssrigen Liisung von HCI und FeCI, in Abh~ngigkeit von den Orienrierungsbeziehungen gemessen. ldeale niederenergetische Korngrenzen zeigten iiberhaupt keine Korntrenzkorrosion. Die Korngrenzkorrosion nahm bis auf den Wert beliebiger Korngrenzen zu, wenn die Abweichung weniger als ein Grad betrug. Der Korrosionsprozess beginnt und erweitert sich in Kanllen entlang von Versetzungen in den Korngrenzen.