The recrystallization behaviour of an AI-Mn alloy containing. a duplex particle structure consisting of a coarse distribution of large cast in inclusions and a finer dispersion of smaller particles due to precipitation prior to recrystallization has been investigated. For a wide range in the fine particle dispersion level. it has been established that the recrystallization reaction is quasi site saturated. A model describing this type of !rain nucleation has been constructed based on the assumption that the finely dispersed particles restrict subgrain growth to grains of larger than average size. By assuming that only these subgrains contribute in the heterogeneous grain nucleation process and by selecting these grains analogous to that of the well-known analysis of abnormal grain growth, an expression has been derived which relates the number of grain nucleation events (nucleation rate) to the particle dispersion and subgrain size distribution. It is further demonstrated that this model is capable of accounting for the experimentally determined relationships between the recrystallized grain size and particle dispersion in the specimens prior to recrystallization.
R&urn&-On a etudie la recristallisation d'un alliage d'Al et de Mn presentant une ripartition irrtguliere de grosses inclusions et une dispersion plus fine de petites particules resultant d'une precipitation avant la recristallisation. Pour une dispersion des fines particules variant dans un large domaine. on a montre que la riaction de recristallisation est pratiquement saturee pour les sites. On a d6velopp2 un modtle pour ce type de germination de grains; il repose sur l'hypothlse qu'une dispersion de fines particules restreint la croissance des sous-grains g des grains de dimension superieure g la moyenne.
En supposant que seuls ces sous-grains participent au processus de germination hitirogkne des grains et en choisissant ces grains de maniere analogue g l'analyse bien connue de la croissance de grains anormale, on a obtenu une relation qui relie le nombre d'tvtnements de germination de grains (vitesse de germination) g la dispersion des particules et & la rtpartition de la taille des sous-grains. On dCmontre Cgalement que ce modile peut rendre compte des relations exp&imentales entre la taille des grains de recristallisation et la dispersion des particules dans les tthantillons avant la recristallisation. Zusammeofassung-Es wurde das Rekristallisationsverhalten einer Al-Mn-Legierung untersucht, die eine zweifache Partikelstruktur aus einer groben Verteilung eingegossener, groDer Einschliisse und einer feineren Verteilung kleiner, vor der Rekristallisation ausgeschiedener Teilchen enthllt. Es ergab sich. da0 die Rekristallisationsreaktion in einem groDen Bereich des Verteilungsniveaus der feinen Partikel quasi-keimgesiittigt ist. Ein Model1 zur Beschreibung dieser Kornbildung wurde aufgestellt aufbauend auf der Annahme, dal3 die fein verteilten Partikel das Wachstum von Subkiirnern zu KGrnern, die gr6Ber als die durchschnittliche GriiDe sind, unterbinden. Mit der Annahme. dal3 nur diese SubkGrner zum heterogenen Keimbildungsprozess beitragen, und mit der Auswahl dieser Kiirner, so wie bei der wohlbekannten Analyse abnormalen Kornwachstums, wird ein Ausdruck hergeleitet, der die Anzahl der Kornbildungsereignisse (Bildungsrate) in Beziehung zu Partikelverteilung und SubkorngrGBe setzt Weiterhin wird dargelegt, dal3 dieses Model1 such die experimentell bestimmten ZusammenhLnge zwischen der GrGDe rekristallisierter Kijrner und der Partikelverteilung in den Proben vor der Rekristallisation erkllren kann.