A sigmoidal reletionship was observed between stmin r&e and stress in the Zn-22 % Al euteotoid alloy, dividing the behavior into three distinct regions. At high strain rates (region III), the activation energy was similar to that, anticipated for lattice diffusion, and the results support the suggestion that the behavior in this region arises from an intragranuler creep process. At intermediate strain rates (region II), the activation energy decreased to a value similar to that anticipated for grain boundary diffusion; whereas at very low strain r&es (region I), the activation energy again increesed to a value close to that for lattice diffusion. This trend was confirmed using two different modes of deformation (tensile and shear) and three different experimental procedures (strain rate cycling, stress cycling and a change in temperature technique). The results suggest that regions I and II arise through the sequential operation of two different processes. ENERGIES D'ACTIVATION ASSOCIEES A L'ECOULEMENT SUPERPLASTIQUE On a observe une relation sigmo7dale entre la vitesse de deformation et le. contr&nte dens I'eutectique Zn-22 % Al; elle divise le comportement de l'alliage en trois regions distinctes. Aux fortes vitesses de deformation (region III), l'energie d'activation est voisine de celle attendue pour la diffusion volumique, et les r&.ultats con5rment que le comportement dans cette region provient d'un processus de fluage intragranulaire. Pour des vitesses de deformation intermediaires (region II), l'energie d'aotivation decroit jusqu'l la valeur attendue pourune diffusion 8UX joints de grains. Pour les faibles vitesses de deformation (region I), l'energie d'activation augmente de nouveau jusqu' Sune valeur proohe de celle de la difYusion volumique. Cette tendance a et6 confkmee en utilisent deux modes de deformation differents (traction et cisaillement) et trois processus experimenteux (cycles de vitasse de deformation, cycles de contrainte et changements de temperature). Ces resultats la&sent & penser que deux processus differents operent Q la suite I'un de l'autre dans les regions I et II. AKTIVIERUNGSENERGIEN BE1 SUPERPLASTISCHEM FLIEDEN In der eutektisohen Legierung aus Zn-22 % Al wurde ein s-formiger Zusammenhang zwischen Abgleitgeschwindigkeit und Spanmmg beobachtet, welcher das Verhalten in drei unterscheidbare Bereiche auf-t&t. Bei hoher Abgleitgeschwindigkeit (Bereich III) war die Aktivierungsenergie &hnlicb der fur Gitterdiffusion erwarteten; die Ergebnisse untersttitzen den Vorschlag, da5 das Verhalten in diesem Bereich von intragranuliiren Kriechprozessen herrtihrt. Bei mittleren Abgleitgeschwindigkeiten (Bereicb 11) fiel die Aktivierungsenergie auf einen Wert iihnlich dem fur Korngrenzendiffusion erwarteten. Dagegen stieg die Aktivierungsenergie bei niedrigen Abgleitgesohwindigkeiten (Bereioh I) wieder auf einen Wert an, der nahe bei dem fiir Gitterdiffusion lag. Diese Tendenz wurde bestSitigt mittels zweier versohiedener Verformungserten (Zug und Soherung) und dreier experimenteller MeDverfahren (Wechsel der Abgleitgeschwindigkeit, der Spammng und der Temperatur). Die Ergebnisse legen nahe, da5 die Bereiche 1 und II von einer Aufeinanderfolge zweier verschiedener Prozesse herriihren.