Synthesis and electrochemical properties of olivine LiFePO4 prepared by a carbothermal reduction method

✍ Scribed by Hui-ping Liu; Zhi-xing Wang; Xin-hai Li; Hua-jun Guo; Wen-jie Peng; Yun-he Zhang; Qi-yang Hu

Publisher
Elsevier Science
Year
2008
Tongue
English
Weight
915 KB
Volume
184
Category
Article
ISSN
0378-7753

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

Improved electrochemical performances of
Improved electrochemical performances of 9LiFePO4Β·Li3V2(PO4)/C composite prepared by a simple solid-state method
✍ J.Y. Xiang; J.P. Tu; L. Zhang; X.L. Wang; Y. Zhou; Y.Q. Qiao; Y. Lu πŸ“‚ Article πŸ“… 2010 πŸ› Elsevier Science 🌐 English βš– 436 KB

9LiFePO 4 β€’Li 3 V 2 (PO 4 ) 3 /C is synthesized via a carbon thermal reaction using petroleum coke as both reduction agent and carbon source. The as-prepared material is not a simple mixture of LiFePO 4 (LFP) and Li 3 V 2 (PO 4 ) 3 (LVP), but a composite possessing two phases: one is V-doped LFP and

Preparation of carbon coated LiFePO4 by
Preparation of carbon coated LiFePO4 by a combination of spray pyrolysis with planetary ball-milling followed by heat treatment and their electrochemical properties
✍ Muxina Konarova; Izumi Taniguchi πŸ“‚ Article πŸ“… 2009 πŸ› Elsevier Science 🌐 English βš– 963 KB

Carbon coated LiFePO 4 could be successfully prepared by a combination of spray pyrolysis (SP) with planetary ball-milling (BM) followed by heat treatment at 500 Β°C. SEM and TEM observations revealed that the carbon coated LiFePO 4 were much smaller in size than the bare LiFePO 4 prepared by the SP

KOH activation of ordered mesoporous car
KOH activation of ordered mesoporous carbons prepared by a soft-templating method and their enhanced electrochemical properties
✍ Jin Jin; Shunsuke Tanaka; Yasuyuki Egashira; Norikazu Nishiyama πŸ“‚ Article πŸ“… 2010 πŸ› Elsevier Science 🌐 English βš– 369 KB

Ordered mesoporous carbon (COU-2) was synthesized by a soft-templating method. The COU-2 mesoporous carbon was activated by using KOH to improve its porosity. The mesopore size of COU-2 was 5.5 nm and did not change by the KOH activation. But, the BET surface area of COU-2 largely increased from 694