One hypereutectic (10% P) and two hypoeutectic (7 and 5S.i P) alloys were investigated with Y//I ratios of 0.35:z.l. Tests were performed in tension. at constant true strain rates in the interval lo-'-3.5 mitt-', and at temperatures from 500 to 600ยฐC. Metallographic analysis showed that the hard, as-extruded /l clusters were dispersed by the deformation, and that the mean phase size increased with strain. Analysis of the metallographic and mechanical data indicated that the strain rate is proportional to the square of the developed stress. and is inversely proportional to the mean phase size and to the square of the x-phase size. An expression is derived for deformation by means of two thermally activated mechanisms operating in series. It is shown that the present results are consistent with such a model in which the accommodation process in the softer y-phase is rate controlling. The influence of the evolving structure on the apparent and instantaneous values of the rate sensitivity and of the activation energy is also discussed.
R&urn&-Un alliage hypereutectique (lo",', P) et deux alliages hypoeutectiques (7 et 5% P) on itt ttudiis, le rapport des phases z et /3 est compris entre 0,35 et 2.1. Des essais de traction a vitesse de deformation constante comprise entre lo-' et 3.5 mn-' ont ite men&s dans un domaine de temperature compris entre 500 et 600% Une etude mttallographique a mis en evidence que les amas resultant du filage de la phase dure /? sont d'ispersef au tours de la deformation et que les tailles movennes des deux phases croissent avec la deformation. Une analyse des don&es provenant de Etude mkallographique et des essais mecaniques a montrt que la vitesse de deformation est proportionnetle au carre de la contrainte et est inversement proportionnelle a la taille moyenne des phases et au carre de la taille moyenne de la phase Y. Une expression est deduite en considerant deux m&can&nes actives agissant en series. I1 est montrt que les resultats de cette etude sont compatibles avec un modtle selon lequel la deformation est contrblte par le mecanisme accommodateur dans la phase z la moins dure. L'influence de I'tvolution de la structure sur les valeurs apparentes et instantaGes du coefficient sensible g la vitesse de deformation et de I'tnergie d'activation sont kgalement discuties.
Zusammenfasung-Eine hypereutektische (IO>; P) und zwei hypoeutektische (7% und 5% P) Leeerungen mit r//l-Verhaltnissen zwischen 0.35 und 2,l wurden untersucht. Versuche-wurden-im ZG bei konstanter wahrer Dehngeschwindiekeit zwischen 10e4 und 3.5 min-i und bei Temwraturen zwischen 500 und 600ยฐC durchgekhrt. Die metallografische Untersudhung zeigte, dal3 die'harten /l-Be&he durch die Verformung zerteilt wurden. und da0 die mittlere PhasengroDe mit der Delmung anstieg. Die Analyse metallografischer und mechanischer Daten weist darauf hin, dal3 die Dehnungsgeschwindigkeit proportional zum Quadrat der sich einstellenden Spannung und umgekehrt proportional zur mittleren PhasengrGBe und zum Quadrat der r-Phasengriige ist. Es wird ein Model1 hergeleitet. das die Verformung mit zwei aufeinanderfolgenden therm&h aktivierten Prozessen beschreibt. Es wird gezeigt, dal3 die vorgelegten Ergebnisse mit einem solchen Model1 vertdglich sind, bei dem der Akkomodationsprozess in der weicheren r-Phase geschwindigkeitsbestimmend ist. AuDerdem wird der EinfluB der entstehenden Struktur auf die scheinbaren und augenblicklichen Werte von Geschwindigkeitsempfndlichkeit und Aktivierungsenergie diskutiert.