Superabsorbent polymeric materials. IV. Swelling behavior of crosslinked poly [sodium acrylate-co-N,N-dimethyl (acrylamidopropyl) ammonium propane sulfonate] in aqueous salt solution

✍ Scribed by Wen-Fu Lee; Pao-Li Yeh

• Publisher: John Wiley and Sons
• Year: 1997
• Tongue: English
• Weight: 226 KB
• Volume: 66
• Category: Article
• ISSN: 0021-8995
• DOI: 10.1002/(sici)1097-4628(19971017)66:3<499::aid-app10>3.0.co;2-r

✦ Synopsis

A series of xerogels based on sodium acrylate (SA), N,N-dimethyl(acrylamidopropyl) ammonium propane sulfonate (DMAAPS), and N,N-methylene bisacrylamide (NMBA) were prepared by inverse suspension polymerization. The water absorbency or swelling behavior for these xerogels in water or various saline solutions was investigated. Results obtained from this study revealed a water absorbency of 721 g H 2 O/g sample in deionized water and 83 g H 2 O/g sample in 0.9 wt % NaCl solution for a gel containing a 1.50 1 10 02 molar fraction of DMAAPS. The absorbency in the chloride salt solutions decreased with an increase in the ionic strength of the salt. For the same ionic strength of various salt solutions, the swelling amount had the following tendency: Co 2/ ú Ni 2/ ú Cu 2/ for the higher ionic strength of 2.44 1 10 05 -1.8 1 10 02 M. The Co 2/ , Ni 2/ , and Cu 2/ solutions induce approximately the same degree of swelling at the lower ionic strength of õ2.44 1 10 05 M. The pH effect on the water absorbency for these xerogels was also investigated.