Sulfate resistance of Portland-pozzolanic cements, prepared by gradual replacement of Portland cement by pozzolana, were studied in relation to their transverse strengths.
Common clay and China clay, after calcination, were used as two different pozzolana.
Strengths of samples, after curing separately in water and in 5% MgSO 4 solution, were measured.
On sulfate-curing thestrength increased remarkably upto a maximum value beyond which it decreased.
This wee thought to be dependent on the mode of formation of ettringite in the set cement.
Strength on water-curing was not much improved.
This was due to the non-availability of lime by the reacting pozzolana because of slower rate of diffusion of lime from the hydrating cement.
Die Sulfat-Widerstandf~higkeit yon Portland-Puzzolan Zementen (mit kalziniertem Ton und Kaolin) wurde hinsichtlich der Biegefestigkeit untersucht. Die Festigkeiten wurden nach getrennter Lagerung in Wasser und in 5~iger MgSO4-LUsu~g gemessen. Nach der Sulfat-Lagerung nahm die Festigkeit bis zu einem Maximalwert zu, um dann wieder abzunehmen. Dieses Verhalten wird mit der Bildung yon Ettringit im gebundenen Zement in Zusammenhang gebracht. Die Wasserlagerung verursachte keine wesentliche Verbesserung der Festigkeit. Dies wurde auf das Fehlen yon Kalk infolge seiner lamgsameren Diffusionsgeschwindigkeit aus dem h2dratierenden Zement zur~ckgefQhrt.