Abstract
The effect of coloring condition of Al with Calcon (sodium 2,2'‐dihydroxy‐azonaphthalene‐4‐sulfonate), on the corrosion resistance of Al in 0.1 M sulfuric acid solution was studied, using cyclic voltammetry and measurement of impedance noise methods. The changes in the corrosion resistance of colored aluminum electrodes were evaluated by measuring the magnitude of impedance and cyclic voltammetric responses of anodized and colored electrodes. An irreversible corrosion response was observed at the cyclic voltammogram of the colored aluminum electrode. The current and threshold potential of corrosion responses strongly depends on the applied conditions during anodizing, coloring and sealing stages. In addition, significant changes in impedance at the ac voltammogram and noise level at some ac frequencies were observed, when the electrodes were colored under various conditions. In this regard, the surface of the electrode was studied by Scanning Electron Microscopy (SEM). Comparison of SEM images of the colored and uncolored aluminum specimens showed that the colored surface contained a significant numbers of pits. The results indicated that coloring aluminum with Calcon could reduce corrosion resistance of aluminum and increase roughness of the oxide film.