Studies on the high electronic energy deposition in polyaniline thin films

✍ Scribed by N.G. Deshpande; Y.G. Gudage; J.C. Vyas; F. Singh; Ramphal Sharma

• Publisher: Elsevier Science
• Year: 2008
• Tongue: English
• Weight: 899 KB
• Volume: 266
• Category: Article
• ISSN: 0168-583X
• DOI: 10.1016/j.nimb.2008.03.087

✦ Synopsis

We report here the physico-chemical changes brought about by high electronic energy deposition of gold ions in HCl doped polyaniline (PANI) thin films. PANI thin films were synthesized by in situ polymerization technique. The as-synthesized PANI thin films of thickness 160 nm were irradiated using Au 7+ ion of 100 MeV energy at different fluences, namely, 5 Â 10 11 ions/cm 2 and 5 Â 10 12 ions/cm 2 , respectively. A significant change was seen after irradiation in electrical and photo conductivity, which may be related to increased carrier concentration, and structural modifications in the polymer film. In addition, the high electronic energy deposition showed other effects like cross-linking of polymer chains, bond breaking and creation of defect sites. AFM observations revealed mountainous type features in all (before and after irradiation) PANI samples. The average size (diameter) and density of such mountainous clusters were found to be related with the ion fluence. The AFM profiles also showed change in the surface roughness of the films with respect to irradiation, which is one of the peculiarity of the high electronic energy deposition technique.