Structure, morphology, and properties of PBZT and methyl pendant PBZT fibers

✍ Scribed by Vinay R. Mehta; Satish Kumar

Publisher
John Wiley and Sons
Year
1999
Tongue
English
Weight
266 KB
Volume
73
Category
Article
ISSN
0021-8995

No coin nor oath required. For personal study only.

✦ Synopsis

The structure, morphology, and properties of the methyl pendant PBZT fiber have been studied with variations in thermomechanical treatment. For comparison, selected studies on PBZT fibers have also been carried out. Crosslinking in the methyl pendant PBZT fiber occurs in the 450 -550Β°C range under free annealing, leading to a nonfibrillar structure. Recoil compressive strength, loop strength, torsional modulus, and the transverse compressive strength of the tension heat-treated MePBZT fiber are 50 to 100% higher compared to the comparably heat-treated PBZT fiber. Compressive strength and other mechanical properties could not be measured on highly crosslinked free annealed samples, as such samples showed significant transverse cracks. Reasons for the development of transverse cracks have been discussed.

πŸ“œ SIMILAR VOLUMES

The effect of coagulant on the structure
The effect of coagulant on the structure and properties of poly(p-phenylene benzobisthiazole) fibers [PBZT]
✍ M. A. Rakas; R. J. Farris πŸ“‚ Article πŸ“… 1990 πŸ› John Wiley and Sons 🌐 English βš– 936 KB

## Abstract Fibers spun from anisotropic solutions of a lyotropic rigid‐rod polymer, poly(para‐phenylene benzobisthiazole) [PBZT], were coagulated into homogeneous nonsolvents including a solution of 18% iodine/82% ethanol, ethanol, and water. The effect of these coagulants on the structure and mec

Morphological structure and mechanical p
Morphological structure and mechanical properties of polyurethane modified with methyl methacrylate
✍ Zheng-Qing Wang; Li-Yi Shi; Zhi-Ping Zhang πŸ“‚ Article πŸ“… 1998 πŸ› John Wiley and Sons 🌐 English βš– 298 KB πŸ‘ 2 views

Three kinds of polyurethane-poly(methyl methacrylate) (PU-PMMA), that is, linear polymer, block copolymer, and interpenetrating polymer network (IPN), were synthesized by a simultaneous polymerization process, respectively. The effects of several factors such as ultraviolet (UV) setting, heat settin

Morphology and Properties of Polyethylen
Morphology and Properties of Polyethylene/Clay Nanocomposite Drawn Fibers
✍ Francesco Paolo La Mantia; Nadka Tzankova Dintcheva; Roberto Scaffaro; Rosamaria πŸ“‚ Article πŸ“… 2008 πŸ› John Wiley and Sons 🌐 English βš– 282 KB

## Abstract The influence of an elongational flow on the morphology of PE/clay nanocomposite drawn fibers was studied. An increase of the elastic modulus and the tensile strength as well as a decrease of the elongation at break are observed with increasing draw ratio. The applied elongational gradi