Solid solutions in the ternary system ZrOz-CeO 2 Y203, by virtue of their high-temperature stability and good electrical conductivity, have potential application in many advanced technologies such as the magnetohydrodynamic ( MHD ) generator. The investigations reported here include studies on the structure, electrical conductiviO, and oxygen ion transport number of solid solutions in the system 0"9{(Zr02)1_ ~ (CeO2)~}--O'I(YzO 3) in the temperature range 1000-1600 K in static air. It is found that electrical conduction proceeds by transport of oxygen ions through the network of oxygen vacancies in the lattice. The variation of conductivity with composition has been analysed in relation to the changes in lattice parameter and scattering of ox)'gen ions.
Mischkristallzusammensetzungen im Dreistoffsystem
ZrOz-CeO 2-Y203 besitzen wegen ihrer Stabilitiit bei hoher Temperatur und ihrer guten elektrischen Lei(f~higkeit in vielen jortschrittlichen Technologien wie dem magnetohydrodynamischen Generator (MHD) m6gliche Anwendungsgebiete. Die hier aufgefiihrten Untersuchungen schlieflen Studien der Struktur, der elektrischen Leitfdhigkeit und der
Transportzahl der Sauersto~onen yon Mischkristallzusammensetzungen im System 0"9 ((ZrO2)l_~-(CeO2)x)-O'l Y203 im Temperaturbereich lO00-1600K h7 stehender Lu[t ein. Die elektrische Leit/~ihigkeit griindet sich auf den Transport yon Sauersto[honen durch die Sauerstoffleerstellen im Atomgitter. Die Abhiingigkeit der Leitfiihigkeit von der Zusammensetzung wurde mit der /l'nderung der Gitterparameter und der Streuung der Sauerstq~onen hi Bezug gesetzt.