The structural changes going on in an Al-Zn (15 at.%) alloy postaged between 125 "C and 215 "C after pre-ageing between 20 "C and 90 "C (till start radii r , = (20 ... 55) A are obtained) were followed by means of XSAS-investigations.The main results are the following:
- An increase of r, does not favour the growth of the precipitates during the reversion treatment. 2. At later reversion times the happening is obviously independent of the pre-history of the samples. 3. The integral intensity is decreasing with increase of T,,,, but the mean distance (d)size (rG) relation between the precipitates is not changed remarkably up to T,,, = 200 "C in the early reversion stage. Conclusions from this behaviour are drawn. Die strukturellen Anderungen in einer AlZn (15 At.-%)Legierung wiihrend Reversionsbehandlungen zwischen 125 "C und 215 "C wurden mittels RKWS-Messungen nach Voralterungen zwischen 20 "C und 90 "C (Startradien 7, = (20 ... 55) A wurden gewiihlt) unteiwicht. Folgende Hauptergebnisse wurden erzielt : 1. Eine Erhohung von rS begunstigt nicht die Wachstumskinetik bei der Reversion. 2. Bei lilngeren Reversionszeiten ist das Geschehen unabhiingig von der Vorgeschichte. 3. Die Integralintensitat nimmt mit zunehmender T,,, ab, aber die Proportionen zwischen mittlerem Partikelabstand (d) und der GroI3e rG) der Ausscheidungen iindern sich nicht merklich bis Tres = 200 "C in den fruhen Stadien der Reversion.
Aus diesen Ergebnissen werden Folgerungen gezogen.