Stress corrosion cracking of X80 pipeline steel in simulated alkaline soil solution

✍ Scribed by Ping Liang; Xiaogang Li; Cuiwei Du; Xu Chen

Publisher
Elsevier Science
Year
2009
Weight
699 KB
Volume
30
Category
Article
ISSN
0261-3069

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

Effect of applied potentials on stress c
Effect of applied potentials on stress corrosion cracking of X70 pipeline steel in alkali solution
✍ Liang Zhang; Xiaogang Li; Cuiwei Du; Yizhong Huang πŸ“‚ Article πŸ“… 2009 πŸ› Elsevier Science βš– 666 KB

Stress corrosion cracking (SCC) behavior of X70 pipeline steel in alkali solution at different applied potentials was investigated using slow strain rate testing (SSRT). Morphology of X70 pipeline steel fracture surface at different applied potentials was observed by scanning electron microscope (SE

Electrochemical corrosion behavior of X8
Electrochemical corrosion behavior of X80 pipeline steel in a near-neutral pH solution
✍ H. B. Xue; Y. F. Cheng πŸ“‚ Article πŸ“… 2010 πŸ› John Wiley and Sons 🌐 German βš– 390 KB

## Abstract In this work, the electrochemical corrosion behavior of X80 pipeline steel was investigated in a near‐neutral pH solution using electrochemical impedance spectroscopy (EIC) and photo‐electrochemical (PEC) measurements as well as X‐ray photo‐electron spectroscopy (XPS) technique. The eff

Stress corrosion cracking of bainite 0.3
Stress corrosion cracking of bainite 0.3C-1Cr-1Mn-1Si-1Ni type steel in acid rain simulated solution
✍ E. Lunarska; K. Nikiforow; E. Sitko πŸ“‚ Article πŸ“… 2004 πŸ› John Wiley and Sons 🌐 German βš– 323 KB

## Abstract The effect of carbon content, heat treatment and surface treatment of high strength aircraft 0.3C‐1Cr‐1Mn‐1Si‐1Ni type steel on susceptibility to pitting corrosion, on hydrogen transport and on hydrogen embrittlement has been studied in acid rain simulated solution. Under open circuit c

Corrosion behavior of API 5L X-60 pipeli
Corrosion behavior of API 5L X-60 pipeline steel exposed to near-neutral pH soil simulating solution
✍ A. Benmoussa; M. Hadjel; M. Traisnel πŸ“‚ Article πŸ“… 2006 πŸ› John Wiley and Sons 🌐 German βš– 166 KB

Steel gas pipelines are exposed externally to damage by surface corrosion and cracking phenomena. They are the main deterioration mechanism under coating failure and cathodic protection (CP) that can reduce the structural integrity of buried gas transmission pipelines where the soil aggressiveness a