Solute-drag effects at migrating diffuse interfaces—II. Experimental investigation of APB migration kinetics and comparison to theory
✍ Scribed by J.E. Krzanowski; S.M. Allen
- Book ID
- 102978070
- Publisher
- Elsevier Science
- Year
- 1986
- Weight
- 888 KB
- Volume
- 34
- Category
- Article
- ISSN
- 0001-6160
No coin nor oath required. For personal study only.
✦ Synopsis
Solute-drag effects at migrating diffuse interfaces have been experimentally examined by studying the migration kinetics of antiphase boundaries at which variations in composition exist. Domain coarsening kinetics in B2 ordered Fe-Al alloys have been measured by transmission electron microscopy for a series of temperatures near the c( + FeAl miscibility gap. Both intrinsic and extrinsic migration behavior were observed, and the intrinsic migration was found to be due to high capillarity driving forces. At lower driving Forces extrinsic migration was observed, and the mobilities were in good agreement with the theoretical predictions presented in the previous paper. In addition. an expression previously presented for predicting the transition to extrinsic behavior was tested and found to successfully predict the transition.
R&urn&-Nous avons etudie experimentalement les effets de trainage de solute sur des interfaces diffuses en tours de migration en etudiant la cinetique de migration des parois d'antiphase sur lesquelles existe une variation de composition. Nous avons mesure par microscopic electronique en transmission la cinetique de grossissement des domaines pour une strie de temperatures au voisinage de la lacune de miscibilite c( + FeAI. Nous avons observe des migrations intrinseques et extrinseques et nous avons trouve que la migration intrinseque etait due a des forces de capillarite importantes. Pour des forces matrices plus faibles, nous avons observe une migration extrinseque et les mobilites etaient en bon accord avec les previsions present&es dans notre article precedent. De plus, nous avons test& une expression present&e anttrieurement; elle permet de prevoir avec sue&s la transition vers le comportement extrindque. Zusammenfassung-Reibungseffekte durch Verunreinigungen an diffusen wandernden GrenzflLchen wurden experimentell untersucht, indem die Wanderungskinetik von Antiphasengrenzen unter Schwankungen der Zusammensetzung gemessen wurde. Mittels Durchstrahlungselektronenmikroskopie wurde die Vergrliberungskinetik der DomPnen in B2-geordneten Fe-Al-Legierungen fiir eine Reihe von Temperaturen in der NIhe der Mischungslticke c( + FeAl gemessen. Es wurde intrinisches und extrinsisches Wanderungsverhalten beobachtet. Das intrinsi~he Verhalten erfoigte wegen hoher Kapillarit~tskr~fte. Bei niedrigeren treibenden Kriiften wurde extrinsische Wanderung beobachtet; die Be~feglichkeiten stimmten mit den theoretischen Voraussagen der vorangehenden Arbeit gut iiberein. Uberdies wurde ein friiher fiir die Voraussage des Uberganges vom intrinsischen zum extrinsischen Wanderungsverhalten angegebener Ausdruck gepriift; er gibt den Ubergang gut wieder.