Solidification of a laser melted nickel-base superalloy

โœ Scribed by Narasimhan, S. L. ;Copley, S. M. ;Stryland, E. W. ;Bass, M.

Book ID
112816479
Publisher
The Minerals, Metals & Materials Society
Year
1979
Tongue
English
Weight
709 KB
Volume
10
Category
Article
ISSN
1543-1916

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

Hot tearing of nickel-based superalloys
Hot tearing of nickel-based superalloys during directional solidification
โœ J. Zhang; R.F. Singer ๐Ÿ“‚ Article ๐Ÿ“… 2002 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 383 KB

The propensity to form cracks during directional solidification was studied in two Ni-based superalloys, CM247LC and IN792 (with varying Ti and Hf contents). Quenching experiments were employed to freeze in the amount of remaining liquid during different stages in solidification. It was found that a

Grain structure development in direction
Grain structure development in directional solidification of nickel-base superalloys
โœ A. Wagner; B.A. Shollock; M. McLean ๐Ÿ“‚ Article ๐Ÿ“… 2004 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 449 KB

The microstructures of three single crystal superalloys (CMSX4, CM186LC and CMSX10) that exhibit quite different casting properties have been characterised quantitatively following quenched directional solidification to identify variations in the grain selection mechanisms. No significant difference