SNMS depth profiling in oxide scales on Fe-20Cr-5Al alloys

✍ Scribed by M. Göbel; G. Borchardt; S. Weber; S. Scherrer

Publisher
Springer
Year
1997
Tongue
English
Weight
80 KB
Volume
358
Category
Article
ISSN
1618-2650

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Deformation of oxide scales on Fe-20Cr a
Deformation of oxide scales on Fe-20Cr alloy under compressive stress
✍ C. H. Zhou; H. T. Ma; L. Wang 📂 Article 📅 2009 🏛 John Wiley and Sons 🌐 German ⚖ 823 KB

## Abstract The behavior of oxide scales on Fe‐20Cr alloy was investigated in constant load at 1173 K in air. The objective was to understand the effect of mechanical loading on the deformation of oxide scales. It was carried out mainly by comparison of surface morphologies of oxidized specimens ob

Void formation and filling under alumina
Void formation and filling under alumina scales formed on Fe–20Cr–5Al based alloys and coatings, oxidised at temperatures up to 1200 °C
✍ D. J. Potter; H. Al-Badairy; G. J. Tatlock; M. J. Bennett 📂 Article 📅 2008 🏛 John Wiley and Sons 🌐 German ⚖ 389 KB

## Abstract During the oxidation, in laboratory air, of thin foils of Fe–20Cr–5Al based alloys, voids were formed in the substrate beneath the outer protective alumina scale after times varying from 50 h at 900 °C to 10 min at 1200 °C. Once the substrate aluminium level had dropped below a critical

Two calculations concerning the critical
Two calculations concerning the critical aluminium content in Fe20Cr5Al alloys
✍ G. Strehl; P. Beaven; B. Lesage; G. Borchardt 📂 Article 📅 2005 🏛 John Wiley and Sons 🌐 German ⚖ 242 KB

## Abstract Alloys for high temperature applications rely on a protective oxide layer formed by selective oxidation. In Fe20Cr5Al type alloys the useful lifetime is governed by the depletion of aluminium by oxidation down to a critical aluminium content. Following spallation of the oxide scale the