Slow growth of isothermal lath martensite in an Fe21N4Mn alloy
✍ Scribed by D-Z Yang; C.M Wayman
- Publisher
- Elsevier Science
- Year
- 1984
- Weight
- 978 KB
- Volume
- 32
- Category
- Article
- ISSN
- 0001-6160
No coin nor oath required. For personal study only.
✦ Synopsis
Laths of martensite in an Fe-21Ni-4Mn alloy form isothermally below room temperature and grow very slowly. Some features of this growth have been observed. Observations were recorded on tine film and the growth characteristics were determined using a frame-by-frame analysis. The lengthening rate of laths formed at -80X has been measured to be about 2.53 x 10-3cm/s, which is IO-* times slower than that of conventional plate martensite. The thickening rate of the laths was found to be about one-tenth the lengthening rate. Both the lengthening and thickening rates of the laths clearly correspond to "slow growing" martensite. To further understand the characteristics of isothermal lath formation, quantitative analysis of data obtained from the tine films was made. The growth activation energy at -8OC was calculated to be about 14,OOOcal!mol. Although precise documentation is lacking, it is inferred that the slow growth rate may be associated with the movement of interfacial dislocations situated at the martensitejaustenite interface. R&u&-Des lattes de martensite se forment de maniere isothenne dans un alliage Fe-2lNi4Mn au-dessous de la temperature ambiante. avec une vitesse de croissance tres lente. Nous avons observe quelques caractiristiques de cette croissance. Nous avons enrigistre nos observations sur film et nous avons determine les caracteristiques de la croissance P l'aide d'une analyse image par image. Nous avons mesure une vitesse d'allongement des lattes d'environ 2.53 x IO-) cm/s a -8oo/,C, ce qui est IO-* fois plus lent que cell de la martensite en plaquettes chessiques. La vitesse d'epaississement da lattes Ctait environ un dixiime de la vitesse d'allongement. Les vitesses d'allongement et d'tpaississement des latta correspondaient toutes deux a une martensite "a croissance Iente". Afin de mieux comprendre les caractetistiques de la formation isotherme des lattes, nous avons effectue une analyse quantitative des donnees obtenues sur films. Nous avons calcule une inergie d'activation de la croissance d'environ 14005 cal/mol a -80°C. Bien que nous manquions de documentation precise, nous pensons que la faible vitesse de croissance pourrait Ctre associte au dtplacement de dislocations interfaciales situ&es a Tinterface martensite/austenite. Zuaunm&rraapMartensitlatten bilden sich in der Legierung Fe-2lNi-4Mn unterhalb Raumtemperatur isotherm und wachsen langsam. Einige Eigenschaften dieses Wachstums wurden untersucht, indem Filmaufnahmen durchgefiihrt und Bild ausgewertet wurden. Die Verliingertmgsrate der Latten be; -8o'C wurde zu 2,53. 10-3cm/s gemessen, welches IO-* der iiblichen Rate ist. Die Geschwindigkeit des Dickenwachstums betrug etwa ein Zehntel der Verliingertmgsrate. Beide Geschwindigkeiten entsprechen eindeutig dem "langsam wachsenden" Martensit. Urn die Charakteristiken der isothetmen Lattenbildung wetter N verstehen, wurden die von den Filmen erhaltenen Daten quantitativ analysiert. Die Aktivienmgsenergie des Wachstums bei -8OC wurde AI etwa 14OOOcal/Mol berechnet. Obwohl ein klarer Beweis fehlt, wird geschlossen, da5 die geringe Wachstumsrate mit der Bewegung von GrenzflPchenversetztmgen an der Fliiche zwischen Martensit und Austenit xusammenhiingt.