β Scribed by W.A Rachinger; A.H Cottrell
No coin nor oath required. For personal study only.
Crystals of ordered beta brass slip along (111); those of ammonium and thallium halides slip along (100). These observations can be interpreted in terms of partial dislocations in the simple cubic lattice of the caesium chloride structure. When the ordering forces are large, these partials are pulled together in pairs by the tension of the superlattice stacking faults between them, and the perfect dislocations thus created can produce slip along (100).
When the ordering forces are small, the partials remain dissociated and can produce slip along ( 111).
An estimate of the critical ordering energy leads to the view that some intermetallic compounds of this crystal type ought to slip along (100). Experiments were made to test this view on various single crystals, the conventional method of slip traces and the prismatic punching method of Smakula and Klein being used to determine the glide elements. The results show that CuZn and AgMg slip along (ill), and that AuCd, AuZn, LiTl, MgTl, Tl(Br, I), and Tl(C1, Br), slip along (100). GLISSEMENTS DANS LES CRISTAVX DV TYPE CHLORURE DE CBSIUM Les cristaux de laiton @ ordonne presentent un glissement le long de (111); ceux des halogenures d'ammonium et de thallium le long de (100). Ces observations sont expliquees par la presence de dislocations partielles dans le reseau cubique simple du type chlorure de cesium. Quand les forces d'ordre sont grandes, ces dislocations partielles se rassemblent par paires sous l'action des "stacking faults" introduits entre elles dans la surstructure et les dislocations parfaites ainsi or&es produisent un glissement le long de (100). Si les forces d'ordre sont faibles, les dislocations partielles restent dissociees et peuvent produire un glissement le long de (111). Une estimation de l'energie d'ordre critique permet de conclure que certains composes intermetalliques de ce type doivent glisser le long de (100). Des experiences ont 6th entreprises pour verifier ce point de vue sur differents monocristaux en utilisant, pour determiner les les elements du glissement, la methode conventionnelle et la methode de poinponnage de Smakula et Klein. Les resultats montrent que CuZn et AgMg glissent le long de (11 l), tandis que AuCd, AuZn, LiTl, MgTl, Tl(Br, I), et Tl(C1, Br) glissent le long de (100). UBER DAS GLEITEN VON KRISTALLEN IN CASIUMCHLORID-STRUKTUR Bei geordneten beta-Messing Kristallen flndet die Gleitung in einer (111).Richtung statt; Ammoniumund Thalliumhalogenide gleiten nach (100). Diese Beobachtungen konnen aufgrund von Teilverstesungen im kubisch primitiven Gitter der Casiumchlorid-Struktur erklart werden. Wenn die ordnenden Krafte gross sind, so werden diese Teilversetzungen durch die Spannung der Uberstrukturstapelfehler au Paaren zusammengezogen. Die dadurch entstehenden vollstandigen Versetzungen konnen dann das Gleiten nach (100) bewirken. Wenn die ordnenden Krafte klein sind, bleiben die Teilversetzungen dissoziiert; sie konnen dann eine Gleitung in der (Ill)-Richtung verursachen. Eine Abschatzung der kritischen Ordnungsenergie ftihrt zu der Ansicht, dass die Gleitrichtung bei einigen intermetallischen Verbindungen dieses Kristalltypus die (lOO)-Richtung sein mtisste. Zur Priifung dieser Ansicht wurden Versuche an verschiedenen Einkristallen ausgefiihrt. Zur Bestimmung der Gleitelemente wurden die iibliche Methode mit Hilfe der Gleitlinienspuren und das Untersuchungsverfahren von Smakula und Klein herangezogen. Die Ergebnisse zeigen, dass CuZn und AgMg nach (111) und dass AuCd, AuZn, LiTI, Tl(Br, I), und TI(C1, Br) nach (100) gleiten. t AeronauticalResearchLaboratories,
π SIMILAR VOLUMES