Sliding behaviour of the 57"(1OiO)I: = 9{1212) y s mmetric tilt boundary has been studied in zinc bicrystals. The bicrystals have been tested under creep at two different rates of intragranular slip (IS). For all the bicrystals, coupled grain boundary sliding (GBS) and migration is observed, the rates of these processes being similar along the boundary. In the vicinity at one end of the boundary, at a slower rate of IS there is no GBS or migration, and at a greater rate of IS they have negative values. Also, the increasing values of GBS and migration from one end of the boundary to the other is observed. The results obtained have been interpreted in terms of behaviour of grain boundary dislocations, produced as a result of interaction between lattice dislocations and the grain boundary. c 1997 Acta Metallurgica Inc.
R&sum&Le comportment de glissement intergranulaire de joint symttrique flexion 57"(10lO)I: = 9{1212} a &t& ttudik dans les bicristaux de zinc. Les bicristaux ont 8ti &udit sous le fluage B deux diffbrentes vitesses de glissement intragranulaire. Les pro& coupI& de glissement intergranulaire et de migration sont observks dans tous ces bicristaux. Les vitesses de ces pro&s sont similaires entre les joints des grains. A une extr&mit& de ce joint et a une vitesse ralentie de glissement intragranulaire, les phtnomtnes de glissement intergranulaire et de migration ne sont pas observts. A une plus grande vitesse de glissement intergranulaire, ces phCnomtnes ont des valeurs ntgatives. La quantiti: de glissement intergranulaire et de migration d'un bord du joint g l'autes augmente. Ces rCsultats peuvent Btre interpr&tks en termes de comportement des dislocations intergranulaire, produites par l'interaction entres les dislocations cristallines et de joint de grain