Role of tail chemistry on liquid and gas transport through organosilane-modified mesoporous ceramic membranes
✍ Scribed by Geoffrey D. Bothun; Katif Peay; Shamsuddin Ilias
- Publisher
- Elsevier Science
- Year
- 2007
- Tongue
- English
- Weight
- 567 KB
- Volume
- 301
- Category
- Article
- ISSN
- 0376-7388
No coin nor oath required. For personal study only.
✦ Synopsis
To develop hydrophobic ceramic membranes, the permeability of liquids (water, ethanol, hexane, and CO 2(l) ) and gases (CO 2 and N 2 ) were examined in unmodified and surface-modified 1 kDa titania and 5 nm ␥-alumina membranes. Octyltrichlorosilane (Cl 3 SiC 8 H 17 ) and its fluorinated analog trichloroperfluorooctylsilane (Cl 3 SiC 2 H 4 C 6 F 13 ) were chosen as modifying agents. SEM/EDS analysis revealed tri-bonding of the silanes to both materials with no evidence of a thick polymerized surface layer. Characterization by CO 2 and N 2 gas permeability indicated Knudsen diffusion in all membranes with minimal CO 2 selectivity, except for 5 nm C8F (CO 2 /N 2 = 2.6) where a surface-flow mechanism was apparent. In contrast, surface modification yielded significant solvent-and modifier-dependent differences in liquid permeability. For example, hexane exhibited the greatest permeability in the C8H mesoporous titania and ␥-alumina membranes, while liquid CO 2 (fluorophilic) permeability was the greatest with the C8F membranes. As expected, the hydrophobic C8F membranes were impermeable to water. Low gas and liquid permeabilities in the C8F-modified membranes were consistent with large transport resistances due to the bulky fluorinated tails. These results demonstrate that silane surface modification can be used to tailor liquid transport behavior and improve apolar solvent flux in ceramic membranes relative to polar solvents. In addition, these membranes have proven amenable to liquid CO 2 , a green solvent alternative.