Short-range order (SRO) kinetics of Ag-(3.5. 7.5. I IS. 15.5) at.% Al have been investigated by measurement of electrical resistivity during isochronal and isothermal annealing. Resides an increase of the atomic mobility with increasing Al-content the samples show a reduction of resistivity with increasing degree of SRO. After a small and sudden temperature change the new equilibrium state of SRO is adjusted by a simple relaxation process with an activation energy of 1.37 + 0. I eV. The microstructure of short-range ordered a-AgAI is thercforc assumed to be homogeneous. R&urn&-Nous avons Ctudie la cinCtique de I'ordre a courte distance (OCD) dans Ag-(3,5; 7.5; I l,5; 15.5) at.% Al par mcsure de la tisistivitk ilcctrique au tours d'un recuit isochrone et isotherme. En plus d'une augmentation de la mobilit& atomique avec la teneur en Al, les tchantillons p&scntaient une diminution de la rbsistiviti lorsqu'on augmentatit le degr6 d'0.C.D. Aprts un petit et brusque changcment de temgrature, on obtient le nouvel &tat d'0.C.D. B l'iquilibre par un simple phCnom&nc de relaxation, avec une inergie d'activation de I.37 f 0,I eV. Nous supposons done que la microctructurc d'AgA1-u ordonnt a courte distance est homog&re. Zusammenfasaung-Die Nahordnungskinetik von Ag-(3,5; 75; ll,5; 15,s) at.% Al wurde durch Messung des elektrischen Widerstandes bei isochroner und isothermer Auslagerung untersucht. Neben einer Zunahme dcr AtommobilitHt mit zunehmendem Al-Gehalt zeigen die Proben eine Widerstandsabnabme mit zunehmendcm Nahordnungsgrad. Nach ciner pliitzlichen kleinen Tempcratur&&rttng stcllt sich das neue Gleichgewicht in &rem einzigen Relaxationsprozeg mit einer Aktivierungscncrgie von 1.37 f 0.1 eV ein. Die Mikrostruktur von nahgeordnetem a-AgAl kann daher als homogen angcnommen we&n.