In this paper, the first stages of the internal oxidation process in silver alloys are studied by residual resistivity and gravimetric measurements, and by transmission electron microscopy. The calorimetric results previously obtained with Ag-Mg alloys have been confirmed. At low temperatures (T < 650Β°C) we show the existence of two stages: first a very fast fixation rate of oxygen, then an ageing of the clusters previously formed, including a very significant increase in the resistivity. An important thermal effect already observed, and fixation of excess oxygen, occur during this later stage. The resistivity reaches a maximum and remains quite large. No clusters are resolvable by electron microscopy, but a great number of dislocations appears. A model of clusters without definite structure and low compactness is proposed. Its relative stability and its non perceptible evolution at low temperatures are explained by the very strong oxygen-metal interactions. At high temperatures (T > 650Β°C) the mechanism is similar: the thermal fluctuation allows an evolution of clusters towards coarse and more compact clusters resolvable by electron microscopy. The resistivity rapidly decreases during ageing. It is likely that these mechanisms can be generalized to other alloys. R&mCDans cet article, nous avons itudie les premiers stades de I'oxydation inteme d'alliages d'argent par des mesures de t&istivitC residuehe et de gravimttrie et par microscopic tlectronique en transmission. Nous avons confirmQ les resultats obtenus anttrieurement par calorimttrie dans des alliages Ag-Mg. A basse temperature (T < 6WC), on observe deux stades: tout d'abord une vitesse de fixation de foxy&e tr&s rapide, ensuite un vieillissement des amas fotmis anterieurement associe a un accroissement significatif de la &istiviti. Au cours de ce demier stage; il y a un effet thermique important deja observe et une fixation de l'oxygene en excb. La r&stivite passe par un maximum et reste trds grande. Nous n'avons pas pu risoudre d'amas par microscopic Bectronique, mais un grand nombre de dislocations apparaissent. Nous proposons pour ces amas un modile de faible compacite, sans structure bien definie. Nous expliquons sa stabilitt relative et son evolution non perceptible a basse temperature par les tr&s fortes interactions oxygirne-metal. Aux temperatures ilevees (T > 65O"C), le mecanisme est semblable: les fluctuations thermiques permettent un grossissement et une augmentation de la compacid dw amas qui deviennent visibles en microscopic 6lectronique. La resistivite diminue rapidement au tours du vieillissement. II est probable que ces mecanismes peuvent se geniraliser a d'autres alliages. Zusammenfassung-In dieser Arbeit werden die Anfangsstadien des inneren Oxidations-prozesses in Silber mit Restwiderstands-, gravimetrischen und elektronenmikroskopischen Messungen untersucht. Die friiher an Ag-Mg-Legierungen erhaltenen kalorimetrischen Ergebnisse konnten bestitigt werden. Rei niedriger Temperatur (T < 650Β°C) gibt es zwei Remiche: zuerst tritt eine sehr hohe Einlagerungsgeschwindigkeit des Sauerstoffes auf, danach eine Alterung der vorher gebildeten Anhiiufungen einschlieglich einer sehr ausgepragten Erhiihung des Widerstandes. Withrend dieses zweiten Bereiches findet sich neben einem schon beobachteten wichtigen thermischen Effekt die Anlagerung von iiberschtissigem SauerstoK Der Widerstand wird maximal und bleibt sehr groB. Im Elektronenmikroskop kiinnen keine Anhlufungen beobachtet werden, jedoch eine gro& Anzahl von Versetzungen. Es wird ein Model1 fur Anhaufungen ohne bestimmte Struktur und mit niedriger Dichte vorgeschlagen. Die relative Stabilitiit und die nicht merkliche Enkwicklung dieser Anhiiufungen bei niedrigen Temperaturen werden mit der sehr starken bindung zwischen Sauerstotf-und Metallatom erkllrt. Bei hoher Temperatur (T > 65OC) ist der Mechanismus Ihnlich: durch die therm&he Fluktuation entwickeln sich grobe und dichtere Anhiiufungen, die im Elektronenmikroskop sichtbar sind. Wiihrend des Alterns sinkt der Widerstand rasch. Vermutlich kiinnen diese Mechanismen verallgemeinert und auf andere Legierungen iibertragen werden.