The intermetallic phases Tb 2 NiAl 4 Ge 2 and Ce 2 NiAl 6-x -Ge 4-y (x ϳ 0.24, y ϳ 1.34) were synthesized in molten Al at temperatures below 1000 °C. Both compounds adopt the tetragonal space group I4/mmm with cell parameters of a ϭ 4.1346(2) A ˚c ϭ 19.3437(7) A ˚for Tb 2 NiAl 4 Ge 2 and a ϭ 4.1951(9) A ˚and c ϭ 26.524(7) A ˚for Ce 2 NiAl 6-x Ge 4-y . The Tb 2 NiAl 4 Ge 2 structure features NiAl 4 Ge 2 layers separated by a double layer of rare earth ions. The Ce 2 NiAl 6-x Ge 4-y (x ϳ 0.24, y ϳ 1.34) structure also contains the NiAl 4 Ge 2 layers along with a vacancy defect PbO-type Al 2-x Ge 2-y layer, and is related to the Ce 2 NiGa 10 structure type.
In flüssigem
Aluminium gebildete quaternäre Germanide: Tb 2 NiAl 4 Ge 2 und Ce 2 NiAl 6-x Ge 4-y (x ϳ 0.24, y ϳ 1.34) Inhaltsübersicht. Die intermetallischen Phasen Tb 2 NiAl 4 Ge 2 und Ce 2 NiAl 6-x Ge 4-y (x ϳ 0.24, y ϳ 1.34) wurden in geschmolzenem Al bei Temperaturen unter 1000 °C synthetisiert. Beide Verbindungen haben die tetragonale Raumgruppe I4/mmm mit den Gitterparametern a ϭ 4,134(2) A ˚, c ϭ 19,3437(7) A ˚für Tb 2 NiAl 4 Ge 2 und a ϭ 4,1951(9) A ˚und c ϭ 26,524(7) A ˚für Ce 2 NiAl 6Ϫx Ge 4Ϫy . Die Struktur von Tb 2 NiAl 4 Ge 2 wird aus NiAl 4 Ge 2 -Schichten, die durch eine Doppelschicht von Seltenerdionen getrennt sind, aufgebaut. Die Ce 2 NiAl 6-x Ge 4-y (x ϳ 0.24, y ϳ 1.34)-Struktur enthält ebenfalls die