Phenol novolac/4βhydroxyphenylmaleimide (HPMI) homopolymer (PHPMI) blends or phenol novolac/HPMIβstyrene copolymer (HPMIβSt) blends were used as the hardener of epoxy resins. Curing behaviour of the above systems and thermal and mechanical properties of the cured epoxy resins were studied. It was not necessary to use a curing accelerator for this system because PHPMI or HPMIβSt had an accelerating effect on the curing reaction. Curing behaviour was investigated by measurement of gelation time(JIS K 6910) and differential scanning calorimetry thermogram (JIS K 7122). Test pieces made from neat resins and from reinforced resins with glass fibre or fused silica were evaluated in terms of thermal and mechanical properties, respectively. It was found that the heat resistance and the mechanical properties improved with increase of PHPMI or HPMIβSt content in the hardener.
π SIMILAR VOLUMES
A new epoxy resin (Bis-ENA) containing naphthalene structure linked with a 1,4-bis(isopropylidene)phenylene was synthesized and was confirmed by elemental analysis, infrared spectroscopy, and 1 H nuclear magnetic resonance spectroscopy. To estimate the effect of naphthalene moiety on the cured polym
A new type of epoxy resin containing 4,4Π-diphenylether moiety in the backbone (2) was synthesized, and was confirmed by gel permeation chromatography, infrared spectroscopy, and 1 H nuclear magnetic resonance spectroscopy. In addition, in order to evaluate the influence of 4,4Π-diphenylether moiety
A new epoxy resin containing the pyrene moiety in the backbone (3) was synthesized and confirmed by gel permeation chromatography and field-desorption mass spectroscopy and infrared spectroscopy. In addition, to evaluate the influence of the pyrene moiety on the structure, epoxy resins having an ant