Corrosion fatigue of a 2024-T3 aluminum
โ
K. -C. Wan; G. S. Chen; M. Gao; R. P. Wei
๐
Article
๐
1995
๐
Springer Netherlands
๐
English
โ 271 KB
It is well accepted that the steady-state fatigue crack growth rates of long cracks depend uniquely on AK for a fixed load ratio R and test environment. Anomalous growth behavior of short cracks in either inert or deleterious environments that has been reported [1-7], however, calls into question th