Preparation of high-modulus nylon 6 fibers by vibrating hot drawing and zone annealing

✍ Scribed by Toshio Kunugi; Kimitaka Chida; Akihiro Suzuki

Publisher
John Wiley and Sons
Year
1998
Tongue
English
Weight
181 KB
Volume
67
Category
Article
ISSN
0021-8995

No coin nor oath required. For personal study only.

✦ Synopsis

To prepare high-modulus fibers, the vibrating hot-drawing and zone-annealing methods have been applied to nylon 6. The vibrating hot drawing was repeated two times, increasing the applied tension; further, the zone annealing was superposed on the vibrating hot-drawn fibers. The superstructure and mechanical properties of each step fiber were investigated. The vibration under a cooperation of heating and tension was very useful for increasing the draw ratio, birefringence, and orientation factor of the amorphous chains. Consequently, the obtained fiber indicated high moduli, namely, Young's modulus of 23 GPa and the dynamic storage modulus at room temperature of 25.3 GPa.

πŸ“œ SIMILAR VOLUMES

Application of CO2 laser heating zone dr
Application of CO2 laser heating zone drawing and zone annealing to nylon 6 fibers
✍ Akihiro Suzuki; Masayoshi Ishihara πŸ“‚ Article πŸ“… 2001 πŸ› John Wiley and Sons 🌐 English βš– 180 KB πŸ‘ 2 views

## Abstract Nlon 6 fibers were zone drawn and zone annealed by using a continuous wave carbon dioxide laser to develop their mechanical properties. A laser‐heating zone drawing was carried out under a applied tension of 35.4 MPa at a power density of 9.65 W Β· cm^βˆ’2^, and then the zone‐drawn fiber w