The porous structures of the highly swollen hydrogels of cellulose-acrylamide graft copolymers were studied by the solute exclusion technique. For these hydrogels, the cumulative volume of pores up to 560 8, in pore width was between 450 and 850 mL/g, and was between 20 and 30% of the total pore volume. With a n increasing in the amount of crosslinker added in the grafting procedure, the cumulative pore volume up to 560 8, decreased. Furthermore, larger pores shrunk preferentially. In the range of concentration from 0.003 to 0.3%, the viscosity of the hydrogels increased remarkably with an increase in concentration. The concentration dependence of the viscosity showed a transition a t about 0.03%, which corresponded to the reciprocal of the water retention values for each copolymer. At concentrations over 3%, fluidity of the hydrogels was lost and the water swollen copolymers became viscoelastic. This dynamic viscoelasticity remained essentially unchanged in the temperature range of 20 to 80Β°C. The dynamic viscoelasticity was dependent on the concentration, but the concentration dependence was smaller than that of the viscosity. The larger the amount of the crosslinker added, the larger the value of dynamic modulus became.