Pit morphology characterization and corrosion fatigue crack nucleation analysis based on energy principle

Fatigue crack propagation estimation of

Fatigue crack propagation estimation of SUS 630 shaft based on fracture surface analysis under pitting corrosion condition

✍ Fong Yuan Ma; Wei Hui Wang 📂 Article 📅 2006 🏛 Elsevier Science 🌐 English ⚖ 872 KB

For the purpose of reducing the diameter and the weight of the propulsion shaft of a high-speed craft, the high strength alloy is normally used. In general, the stainless SUS 630 is selected as the shafting material. While pitting corrosion existed in such kind material can be a problem to considera