The phase relation in AgZn-AgMg quasibinary alloys (Ag~&j~_,Mg, ternary alloys) was studied by high-temperature X-ray diffractometry and differential thermal analysis.
The c-phase (complex hexagonal structure) which exists at low temperature in a terminal binary alloy AgZn disappears when Zn atoms of a few at. Y0 are replaced by Mg atoms. On the other hand, the p-phase (CsCt-type ordered structure) which is a stable phase of another terminal alloy AgMg extends to all the remaining composition. The transition temperature from the p-phase to a b-phase (b.c.c. disordered structure) rises up rapidly with the increase of Mg content and the F-phase becomes stable up to melting point in a composition range of more than about 25 at. % Mg. Further. a Heusler-type ordered phase appears at low temperature around a stoichiometric composition of Ag,ZniMg. The critical temperature between the Heusler-and /Y-phases has a maximum (523 K) near the stoichiometric composition.
The superlattice formation of Ag?ZnMg was discussed on a basis of the pseudopotential method For this purpose, an expression of the structure-dependent energy was given for the ternary alloy-AglZnMg. The numerical result explained satisfactorily the existence of the two types of ordered phase.
R&urn&-On a Ctudie les relations entre phases dans des alliages pseudobinaires AgZn-AgMg (alliages ternaires Ags,ZnSO_.Mg,) par diffractomitrie de rayons X a haute temperature et par analyse thermique difl'erentielle.
La phase { (structure hexagonale complexe). qui existe a basse temperature dans un alliage terminal binaire AgZn, disparait forsqu'on remplace quelques at. % d'atomes de Zn par des atomes de Mg. Au contraire, la phase 8' (structure ordonnee du type CsCi), qui est stable dans un autre alliage terminal AgMg, s'etend aux alliages de toutes les autres com~sitions. La temperature de transition de la phase /3' a la phase fi (structure cc, dbordonnee) augments rapidement avec la teneur en hfg et la phase @' devient stable jusqu'au point de fusion au dessus de 25 at. "/:, Mg. De plus, une phase ordonnee analogue a I' alliage de Heussler apparait a basse temperature autour de la composition stoechiomttrique Ag,ZnMg. La temperature critique entre les phases de Heussler et /I' passe par un maximum (523 K) pres de la composition stoechiomttrique.
On discute de la formation de la surstructure Ag,ZnMg par une methode de pseudopotentiels. Pour cela, on donne une expression de la partie de l'energie qui depend de la structure pour l'alliage ternaire AgsZnMg. Les r&hats numeriques permettent d'expliquer de man&e satisfaisante i'existence des deux types de phases or donnees.
Zusammenfassung-Mit
Rontgendiffraktometrie bei hohen Temperaturen und differentieller therm&her Analyse wurden die Phasenverhlltnisse in den quasibinfren Legierungen AgZn-AgMg (tern&e Legierungen Ag,,ZnSO_xMg,) untersucht. Die <-Phase (komplexe hexagonale Struktur). die bei niedrigen Temperaturen in der bin&en Grenzlegierung AgZn existiert. verschwindet. wenn einige wenige At. O0 Zn-Atome durch Mg-Atome ersetzt werden. Andererseits dehnt sich die F-Phase (geordnete Struktur vom CsCl-Typ), die eine stabile Phase einer anderen Grenziegierung, AgMg. ist, iiber s;imtliche Zusammensetzungen aus. Die Ubeqangstemperatur von der P-Phase zur B-Phase (kn. entordnete Struktur) steigt rasch an mit ansteigendem Mg-Gehalt. Die F-Phase wird stabil bis zum Schmetzpunkt im Zu~mmense~ungs~re~ch mit mehr als 25 At. Y0 Mg. AuDerdem tritt bei niederer Temperatur in der Umgebung der stochiometrischen Zusammensetzung von Ag>ZnMg eine geordnete Phase vom Heusler-Typ auf. Die kritische Temperatur zwischen der Heusler-und der F-Phase erreicht ein Maximum (523 K) in der Nlhe der stijchiometrischen Zusammensetzung. Die Uberstrukturbildung von Ag:ZnMg wird auf der Grundlage der Pseudopotentialmethode diskutiert. Dazu wird ein Ausdruck der strukturabhlngigen Energie fur die ternare Legierung AglZnMg angegeben. Das numerische Ergebnis erklart die Existenz der zwei Typen geordneter Phasen zufriedenstellend.