Parametric evaluation of susceptibility of CuNi alloys to sulfide-induced corrosion in sea water

Book ID: 123060431
Publisher: Elsevier Science
Year: 1979
Weight: 84 KB
Volume: 26
Category: Article
ISSN: 0198-0254
DOI: 10.1016/0198-0254(79)90694-0

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Effects of benzotriazole on the corrosio

Effects of benzotriazole on the corrosion of Cu10Ni alloy in sulfide-polluted salt water

✍ N.K. Allam; E.A. Ashour; H.S. Hegazy; B.E. El-Anadouli; B.G. Ateya 📂 Article 📅 2005 🏛 Elsevier Science 🌐 English ⚖ 334 KB

Effect of sulfide ions on the corrosion

Effect of sulfide ions on the corrosion behaviour of Al–brass and Cu10Ni alloys in salt water

✍ S.M Sayed; E.A Ashour; G.I Youssef 📂 Article 📅 2003 🏛 Elsevier Science 🌐 English ⚖ 772 KB

The relationship between the characteris

The relationship between the characteristics of oxide film and stress corrosion susceptibility of NiCrFe alloy in high temperature water

✍ Hideo Hirano; Hiroshi Takaku; Tatsuo Kurosawa 📂 Article 📅 1990 🏛 Elsevier Science 🌐 English ⚖ 345 KB

Promoting effect of low concentration of

Promoting effect of low concentration of benzotriazole on the corrosion of Cu10Ni alloy in sulfide polluted salt water

✍ Nageh K. Allam; Elsayed A. Ashour 📂 Article 📅 2008 🏛 Elsevier Science 🌐 English ⚖ 681 KB

Effect of sulfide ions on the stress cor

Effect of sulfide ions on the stress corrosion behaviour of Al-brass and Cu10Ni alloys in salt water

✍ S. M. Sayed; E. A. Ashour; G. I. Youssef; S. M. El-Raghy 📂 Article 📅 2002 🏛 Springer 🌐 English ⚖ 289 KB

Effect of heat treatments on Cu-Ni 70/30

Effect of heat treatments on Cu-Ni 70/30 alloy pitting susceptibility in sea water at different temperatures

✍ A. M. Beccaria; G. Poggi; Y. Z. Wang 📂 Article 📅 1994 🏛 John Wiley and Sons 🌐 German ⚖ 891 KB

## Abstract A series of experiments was carried out on Cu‐Ni 70/30 commercial alloy specimens presenting different microstructures. The microstructure of homogeneized specimens was modified with annealing treatments by which grain size significantly increased and intermetallic compounds precipitate