Orientation dependence of metal dusting nanoprocesses on nickel single crystals
✍ Scribed by Q. Wei; E. Pippel; J. Woltersdorf; S. Strauß; H. J. Grabke
- Publisher
- John Wiley and Sons
- Year
- 2000
- Tongue
- German
- Weight
- 320 KB
- Volume
- 51
- Category
- Article
- ISSN
- 0947-5117
No coin nor oath required. For personal study only.
✦ Synopsis
Nanoprocesses of metal dusting have been studied on nickel single crystal surfaces by TEM and AEM techniques. The samples had been exposed to strongly carburizing conditions (a C b 1) for 4 h at 650 8C. On Ni(111) and Ni(110) epitaxial growth of graphite was observed, graphite layers with their basal planes had grown parallel to the surface and there was no indication of metal dusting attack. In contrast, on Ni(100) metal dusting had started by inward growth of graphite lattice planes oriented more or less vertically to the surface.
Unter
Verwendung von TEM-und AEM-Techniken wurden die Nanoprozesse des Metal Dusting auf Nickel-Einkristalloberfla Èchen untersucht. Die Proben wurden einer stark aufkohlenden Atmospha Ère (a C b 1) fu Èr 4 Stunden bei 650 8C ausgesetzt. Auf Ni(111) und Ni(110) wurde epitaktisches Wachstum von Graphit beobachtet, wobei die Graphitbasisebenen parallel zur Oberfla Èche liegen und kein Metal Dusting auftritt. Im Gegensatz dazu begu Ènstigen die mehr oder weniger senkrecht in die Ni(100)-Oberfla Èche einwachsenden Graphitgitterebenen den Metal-Dusting-Prozess.