The elaboration of cordierite powders from aqueous or alcoholic solutions, gelled by organic polymers, has been studied. The aqueous solution, made from Al and Mg nitrates or citrates and Si alkoxide, tetraethylorthosilicate ( TEOS) or 3-( triethoxysilyl)propylamine ( TESPA ), is gelled by polyacrylamide and the aqueous gel is calcined at 750Β°C. The behaviour of the powder depends strongly on the precursor solution. A powder produced from citrates and TESPA expands upon sintering to a porous cordierite, while that elaborated from nitrates and TEOS densities completely before crystallizing into #-and then ~-cordierite.
In the same way, an ethanolic solution of nitrates and TEOS, gelled by poly(2-hydroxyethyl methacrylate) (pHEMA ) produces a very homogeneous powder that densities completely; ct-cordierite is obtained at a particularly low temperature ( IO00Β°C). propylamin ( TESPA ) hergestellt wurden, wurden mit Polyacrylamid geliert. Dieses w6ssrige Gel wurde bei 750Β°C kalziniert. Das Verhalten der Pulver hiingt in groriem Marie yon der verwendeten Ausgangsl6sung ab. Pulver, die aus Zitraten und TESPA gewonnen wurden, dehnten sich beim Sintern aus und bildeten por6sen Cordierit. Jene aus Nitrat und TEOS verdichten v6llig, ehe sie zu I~-und anschlieriend zu ~-Cordierit kristallisierten, In analoger Weise ergab eine L6sung aus Nitraten und TEOS in ~t'thanol, die mit Poly(2-hydroxyiithyl methacrylat) (pHEMA) geliert wurde, ein sehr homogenes Pulver das v61lig verdichtete. Bereits bei sehr niedrigen Temperaturen ( IO00Β°C) bildete sich ~-Cordierit.
Die Herstellung yon Cordieritpulvern aus wiissrigen oder alkoholischen L6sungen, die durch Zugabe organischer Polymere gelierten, wurde untersucht. Wgissrige L6sungen, die aus Al-und Mg-Nitraten oder -Zitraten und