An X-ray study has been made of the change of degree of order and domain size during the isothermal ordering of a series of N&Fe, Ni,Mn and Cu,Au alloys, all of which form the same type of superlattice.
It is shown that the ordering process varies with composition within an alloy system as well as from one alloy system to another.
Hardness measurements were made upon the same samples as used in the X-ray investigation.
From this combined X-ray and mechanical properties study it is concluded that an initial increase in strength during isothermal ordering is due to a combination of short range order strengthening and the strengthening produced when an antiphase boundary has to be created. a new strengthening mechanism involving the cutting of ordered domains by single dislocations is shown to contribute t)o this initial increase in strength. After a continuous domain structure has developed, a soft,ening, as predicted by Cottrell and Flinn, is observed. DURCISSEMENT PAR APPARITION D'ORDRE ET PAR L'EFFET DE TAILLE DES DOMAINES PAR DES ALLIAGES A SURRESEAU DU TYPE Cu,Au Les auteurs ont &tudi8 par diffraction de rayons X, les modifications des degr& d'ordre et de la taille des domaines pendant un recuit isotherme approprib d'une &rie d'alliages de Ni,Fe Ni,Mn et Cu,Au, formant tous un surreseau similaire. On montre que la modification d'ordre depend de la composition pour un alliage mbtallique d&ermine aussi bien que de la nature de l'alliage mbtallique. I.es mesures ont BtB effectuees sur les Bchantillons utili&s pour la diffraction des rayons X. La comparaison des rBsultats obtenus pour les propri&% mbcaniques et par I'Btude par rayons X permet de conclurr que l'accroissement initial de la resistance au cows du traitement isotherme est dfi Q la combinaison des effets d'apparition d'ordre B petite distance et de la formation de joints antiphases. Les auteurs demontrent qu'un nouveau mkcanisme de durcissement justifie l'accroissement initial de la rBsistance; il fait intervenir le sectionnement des domaines ordonnbs par des dislocations. Lorsque la structure B domaine continu s'est d&elopp&e, on observe l'adoucissement pr&vu par CoWell et Flinn. ORDNUNG UND ANTIPHASENBEREICHS-HARTUNG BE1 LEGIERUNGEN MIT CU,AU-CBERSTRUKTUR Die Anderung des Ordnungsgrades und der BereichsgrGBe w&hrend ,$er isothermen Ordnung einer Reihe van N&Fe-, Ni,Mn-und Cu,Au-Legierungen, die alle die gleiche Uberstruktur haben, wurde mit Rantgenmethoden untersucht. Der OrdnungsprozeD iindert Bich sowohl mit der Zusammensetzung innerhalb eines Legierungssystems wie van einer Legierung zur anderen. Hilrtemessungen wurden an den gleichen Proben wie die RGntgen-Messungen angestellt. Aus der gleichzeitigen Untersuchung der rentgenographischen und der mechanischen Eigenschaften wird geschlossen, da0 die anfiingliche Festigkeitszunahme w&hrend der isothermen Ordnung auf einer Kombination van Nahordnungs-Verfestigung und der durch die Erzeugung van Antiphasen-Grenzen bedingten Verfestigung beruht. Es wird gezeigt, daB zu dieser anflinglichen Festigkeitszunahme ein neuer Verfestigungsmechanismus beitriigt, und zwar das Schneiden geordneter Bereiche durch einzelne Versetzungen. Nach der Entwicklung einer gleichfiirmigen Bereichsstruktur wird entsprechend der Vorhersage van Cottrell und Flinn rine Knt'festigung beobachtet.
Cu,Au type alloys by a process of nucleation and *