Capillary pressure and plastic shrinkage have been measured simultaneously. The action of capillary pressure in fresh concrete is assumed to be the cause of plastic shrinkage. Characteristic results are presented to verify the essential statements of this hypothesis. The influence of water-cement ratio on plastic shrinkage is dealt with in moredetail.
It is shown that plastic shrinkage leads to highest contraction of fresh concrete in the range 0,5< W/C < 0,6. Rewetting the dried surface stops immediateTy further contraction. The influence of additives on plastic shrinkage is mentioned and discussed on the basis of the presented results.
Zun~chst warden einige grunds~tzliche Oberlegungen zur Wirkun Z des Kapillardruckes auf des Verhalten des Frischbatons angestellt. In Form einer Arbeitshypothese wird der Kapillardruck in urs~chlichen Zusammenhang mit dem FrOhschwinden des Frisohbetons gebracht. Einige charakteristische Ergebnisse, die diese Hypothese s~Otzen, warden beschrieben. Der EinfluB des Wasser/Zement-Verh~Itnisses BUr des FrOhschwinden wurde genau studiert. Im Bereich zwischen W/Z-0,5 und W/Z=0,6 wird maximale Kontraktion beobachtet. Oas FrOhschwinden wird durch Wiederbefeuchtung einer zetrockneten Betonoberfl~che sofort zum Stillstand gebracht. Oar EinfluB von VerflOssigern BUr des FrOhschwinden wird diskutiert.