On slip-induced intergranular cavitation during low-cycle fatigue of nickel at intermediate temperature
✍ Scribed by L.C. Lim; R. Raj
- Publisher
- Elsevier Science
- Year
- 1984
- Weight
- 855 KB
- Volume
- 32
- Category
- Article
- ISSN
- 0001-6160
No coin nor oath required. For personal study only.
✦ Synopsis
Intergranular cavitation has been observed in nickel during low-cycle fatigue at temperatures and strain-rates where there was little or no grain boundary sliding. The cavities were found to nucleate early in fatigue life and were associated with impinging crystal-slip traces at the boundaries. Implication of this mechanism in low-cycle fatigue failure at intermediate temperature is also discussed. R&WI&-Nous avons observe la cavitation intergranulaire dans le nickel au tours de la fatigue I faible nombre de cycles pour des temperatures et des vitesses de difotmation ou il y avait peu ou pas de glissement intergranulaire. Les cavites germaitnt tot dans la durCe de vie en fatigue et elles Ctaient associks a des traces de glissement ctistallin arrivant sur les joints. Nous discutons Cgalement da implications de ce m&anisme pour la rupture en fatigue a faible nombre de cycles 1 une temperature intermtdiaire. maaanng-In Nickel wurde wiihrend der Ermiidung mit geringen Zyklenzahlen bei Temperaturen und Dehnungsraten, bei denen wenig oder kein Komgrenzgleiten auftritt, intergranulare Hohlraumbildung beobachtet. Die Hohlriiume bilden sich friih wiihrend da Ermiidung und hlngen mit Stellen zusammen, an denen Gleitzonen in den Kbmim auf die Komgrenzen sto&n. Die Bedeutung dieses Mechanismus fib den Ermiidungsbruch bei kleinen Zyklenzahlen und mittleren Temperaturen wird diskutiert.