On factors influencing the ductile-to-brittle transition in a bulk metallic glass
โ Scribed by R. Raghavan; P. Murali; U. Ramamurty
- Publisher
- Elsevier Science
- Year
- 2009
- Tongue
- English
- Weight
- 731 KB
- Volume
- 57
- Category
- Article
- ISSN
- 1359-6454
No coin nor oath required. For personal study only.
โฆ Synopsis
An experimental study to ascertain the ductile-to-brittle transition (DBT) in a bulk metallic glass (BMG) was conducted. Results of the impact toughness tests conducted at various temperatures on as-cast and structurally relaxed Zr-based BMG show a sharp DBT. The DBT temperature was found to be sensitive to the free-volume content in the alloy. Possible factors that result in the DBT were critically examined. It was found that the postulate of a critical free volume required for the amorphous alloy to exhibit good toughness cannot rationalize the experimental trends. Likewise, the Poisson's ratio-toughness correlations, which suggest a critical Poisson's ratio above which all glasses are tough, were found not to hold good. Viscoplasticity theories, developed using the concept of shear transformation zones and which describe the temperature and strain rate dependence of the crack-tip plasticity in BMGs, appear to be capable of capturing the essence of the experiments. Our results highlight the need for a more generalized theory to understand the origins of toughness in BMGs.
๐ SIMILAR VOLUMES
We provide a quantitative account of the shear-banding behavior in Mg-based bulk metallic glasses. Microcompression experiments showed that shear bands propagated in an intermittent manner at the micron and submicron scales. The shear-banding kinetics involves competition between shear-induced softe
Attention is called to a new phenomenon: in certain materials, specimen size (or, its energy-storage capacity) influences its brittle-ductile transition and strength. This effect is not the recognized statistical one (which only concerns the nucleation of fracture), blot derives from the strain-ener