Neutron powder diffraction studies in CaMn1-xCuxO3 (x = 0, 0.2)

✍ Scribed by S. Ravi; Manoranjan Kar; S. M. Borah; P. S. R. Krishna

• Publisher: John Wiley and Sons
• Year: 2008
• Tongue: English
• Weight: 149 KB
• Volume: 43
• Category: Article
• ISSN: 0232-1300
• DOI: 10.1002/crat.200800407

✦ Synopsis

Neutron powder diffraction patterns were recorded on CaMn 1-x Cu x O 3 (x = 0 and 0.20) compounds at different temperatures down to 11K. All the patterns were analyzed by employing Rietveld refinement technique and using the Fullprof program. The observed crystallographic peaks could be refined by using Pbnm space group and no structural transition has been observed down to 11K. An additional peak at 2θ = 16.7° has been observed with decrease in temperature below T N and its intensity was found to increase with decrease in temperature. It could be indexed to magnetic (101) plane. The magnetic ordering is found to be G-type antiferromagnetic behaviour. The magnetic moment at 11K for the samples x = 0.0 and 0.20 are found to be 2.69 and 2.42μ B . The doped Cu ions are found to be in Cu 2+ state and take part antiferromagnetic interactions with Mn ions.