Morphology of Si surfaces sputter-eroded by low-energy Xe-ions at glancing incident angle
✍ Scribed by K. Zhang; H. Hofsäss; F. Rotter; M. Uhrmacher; C. Ronning; J. Krauser
- Publisher
- Elsevier Science
- Year
- 2009
- Tongue
- English
- Weight
- 999 KB
- Volume
- 203
- Category
- Article
- ISSN
- 0257-8972
No coin nor oath required. For personal study only.
✦ Synopsis
Sputter erosion of Si generates nanoscale ripple patterns which are stable at ambient conditions and which may serve as an experimental test of ripple formation theories. Up to now, almost all studies on ripple formation of Si-surface have been carried out with large ion-fluence (varying from 10 17 ions/cm 2 to 10 22 ions/cm 2 ) and shown the ripple-pattern orientated in the direction perpendicular to the ion-beam. The present reports on the evolution of Si surfaces after low-energy (5 keV) Xe + ion irradiation at room temperature with low ion-fluences of 1 × 10 14 -3 ×10 17 ions/cm 2 at glancing incident angles θ up to 85°. The purpose is to focus on the critical angle θ c of the ripple rotation from perpendicular to parallel orientation to the ion beam. It is found that the nanometer ripple formations occurred for θ ≥ 70°with an orientation perpendicular (for 80°N θ ≥ 70°) or parallel (for θ N 80°) to the ion-beam direction. At the critical angle θ c = 80°ion-bombardment produced two-dimensional nanopatterns with tile-like laminas. The size of the laminas increase by raising the ion-fluences. The surface roughness obeys an exponential function (ω ~exp (R k •Φ)) for ion-fluences Φ b 1.5 × 10 16 ions/cm 2 , while for larger ion-fluences the roughness nearly reaches saturation and only increases slowly according to a power law function ω ~Φβ with β ≈ 0.34.