Morphological change in FePt nanogranular thin films induced by swift heavy ion irradiation

✍ Scribed by M. Shirai; K. Tsumori; M. Kutsuwada; K. Yasuda; S. Matsumura

• Publisher: Elsevier Science
• Year: 2009
• Tongue: English
• Weight: 685 KB
• Volume: 267
• Category: Article
• ISSN: 0168-583X
• DOI: 10.1016/j.nimb.2009.03.079

✦ Synopsis

We have investigated morphology change of FePt nanogranular films (FePt) 47 (Al 2 O 3 ) 53 under irradiation with 210 MeV Xe ions. Here, electron tomography technique was extensively employed to clarify threedimensional (3D) structure in irradiated specimens, in addition to conventional transmission electron microscopy (TEM) techniques such as bright-field observation and scanning TEM energy dispersive Xray spectroscopy (STEM-EDX) analysis. The ion irradiation induces the coarsening of FePt nanoparticles with elongation along the beam direction. Electron tomography 3D reconstructed images clearly demonstrated that when the fluence achieves 5.0 Â 10 14 ions/cm 2 , well-coarsened FePt balls have been formed on the irradiated surface, and the particles in the film interior have been deformed into rods along the ion trajectory. The alloy particles become inhomogeneous in composition after prolonged irradiation up to 1.0 Â 10 15 Xe ions/cm 2 . The particle center is enriched with Pt, while Fe is slightly redistributed to the periphery.